An interpoly-stacked dielectric film with a SiO2/Si3N4/SiO2/Si (ONO) structure was prepared via the atomic-layer deposition method. The multilayer structure of the ONO film with triple interfaces was investigated via medium-energy ion scattering (MEIS). A few defects in the interface layer of the ONO structure were detected. From the X-ray photoelectron spectroscopy (XPS) results, it was presumed that the interface layer with defects in the MEIS result is due to the formation of an oxynitride layer on the unstable and rougher Si3N4 layer via. By measuring the I-V characteristics, the leakage current density and breakdown field of the ONO film were determined to be 3.4 x 10(-9) A/cm2 and 10.86 MV/cm, respectively. By estimation the C-V curve, the flat band (V(FB)) of the ONO film shifted to a negative voltage (-1.14 V), the dielectric constant (K(ONO)) of the ONO film was 5.79, and the effective interface-trapped charge density of the ONO film was about 4.96 x 10(11)/cm2.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.