PURPOSEThis study was conducted to evaluate clinical validity of a zirconia full-coverage crown by comparing zirconia's wear capacity over antagonistic teeth with that of feldspathic dental porcelain.MATERIALS AND METHODSThe subject groups were divided into three groups: the polished feldspathic dental porcelain group (Group 1), the polished zirconia group (Group 2), and the polished zirconia with glazing group (Group 3). Twenty specimens were prepared from each group. Each procedure such as plasticity, condensation, and glazing was conducted according to the manufacturer's manual. A wear test was conducted with 240,000 chewing cycles using a dual-axis chewing simulator. The degree of wear of the antagonistic teeth was calculated by measuring the volume loss using a three-dimensional profiling system and ANSUR 3D software. The statistical significance of the measured degree of wear was tested with a significant level of 5% using one-way ANOVA and the Tukey test.RESULTSThe degrees of wear of the antagonistic teeth were 0.119 ± 0.059 mm3 in Group 1, 0.078 ± 0.063 mm3 in Group 3, and 0.031 ± 0.033 mm3 in Group 2. Statistical significance was found between Group 1 and Groups 2 and between Group 2 and 3, whereas no statistical significance was found between Group 1 and Group 3.CONCLUSIONDespite the limitations of this study on the evaluation of antagonistic teeth wear, the degree of antagonistic tooth wear was less in zirconia than feldspathic dental porcelain, representing that the zirconia may be more beneficial in terms of antagonistic tooth wear.
Objective This study investigated the marginal and internal adaptation of individual dental crowns fabricated using a CAD/CAM system (Sirona’s BlueCam), also evaluating the effect of the software version used, and the specific parameter settings in the adaptation of crowns.Material and Methods Forty digital impressions of a master model previously prepared were acquired using an intraoral scanner and divided into four groups based on the software version and on the spacer settings used. The versions 3.8 and 4.2 of the software were used, and the spacer parameter was set at either 40 μm or 80 μm. The marginal and internal fit of the crowns were measured using the replica technique, which uses a low viscosity silicone material that simulates the thickness of the cement layer. The data were analyzed using a Friedman two-way analysis of variance (ANOVA) and paired t-tests with significance level set at p<0.05.Results The two-way ANOVA analysis showed the software version (p<0.05) and the spacer parameter (p<0.05) significantly affected the crown adaptation. The crowns designed with the version 4.2 of the software showed a better fit than those designed with the version 3.8, particularly in the axial wall and in the inner margin. The spacer parameter was more accurately represented in the version 4.2 of the software than in the version 3.8. In addition, the use of the version 4.2 of the software combined with the spacer parameter set at 80 μm showed the least variation. On the other hand, the outer margin was not affected by the variables.Conclusion Compared to the version 3.8 of the software, the version 4.2 can be recommended for the fabrication of well-fitting crown restorations, and for the appropriate regulation of the spacer parameter.
While zirconium oxide coping material alone has a degree of masking ability, the resulting color of a restoration can be further modified with the veneering porcelain.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.