Through loading of TiO2 on the surface of K6SiW11O39Co(II)(H2O)·xH2O (SiW11Co), a novel photoanode material has been created for dye-sensitized solar cells (DSSC). The absorbing band as well as photoelectricity response range of TiO2@SiW11Co is extended to the visible range. In addition, the absorption in the UV range is enhanced notably compared with P25 (raw TiO2). More importantly, the recombination of the TiO2 network is avoided. TiO2@SiW11Co is mixed with P25 powder (wt ∼1 : 1) to assemble dye-sensitized (N719) solar cells, which exhibit a short-circuit photocurrent density as high as 18.05 mA cm(-2), which is 64% higher than blank samples under the standard AM1.5G global solar irradiation. In addition, the mechanisms for SiW11Co in DSSC are proposed.
The thermally conductive structural film adhesive not only carries large loads but also exhibits excellent heat-transfer performance, which has huge application prospects. Herein, a novel epoxy (Ep) thermally conductive structural film adhesive was prepared using polyphenoxy (PHO) as the toughening agent and film former, boron nitride (BN) nanosheets as the thermally conductive filler, and polyester fabric as the carrier. When the amount of PHO in the epoxy matrix was 30 phr and the content of nano-BN was 30 wt.% (Ep/PHO30/nBN30), the adhesive resin system showed good film-forming properties, thermal stability, and thermal conductivity. The glass transition temperature of Ep/PHO30/nBN30 was 215 °C, and the thermal conductivity was 209.5% higher than that of the pure epoxy resin. The Ep/PHO30/nBN30 film adhesive possessed excellent adhesion and peeling properties, and the double-lap shear strength at room temperature reached 36.69 MPa, which was 21.3% higher than that of pure epoxy resin. The double-lap shear strength reached 15.41 MPa at 150 °C, demonstrating excellent high temperature resistance. In addition, the Ep/PHO30/nBN30 film adhesive exhibited excellent heat-aging resistance, humidity, and medium resistance, and the shear strength retention rate after exposure to the complicated environment reached more than 90%. The structural film adhesive prepared showed excellent fatigue resistance in the dynamic load fatigue test, the double-lap shear strength still reached 35.55 MPa after 1,000,000 fatigue cycles, and the strength retention rate was 96.9%, showing excellent durability and fatigue resistance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.