Melt-spun fibers were made from poly(ε-caprolactone) (PCL) coalesced from stoichiometric inclusion complex crystals formed with host urea. Melting and crystallization behaviors, mechanical properties, and the birefringence of undrawn and cold-drawn fibers were investigated. Undrawn coalesced PCL fibers were observed to have 500-600% higher moduli than undrawn as-received (asr) PCL fibers and a modulus comparable to drawn asr PCL fibers. Drawn coalesced PCL fibers have the highest crystallinity, orientation, and 65% higher moduli than drawn asr PCL fibers. Drawn coalesced PCL fibers have only a 5% higher crystallinity than drawn asr PCL fibers, yet they have 65% higher moduli and lower elongation at break values. Clearly, the intrinsic alignment of the coalesced polymers is the reason for their higher moduli and lower elongation, as confirmed by the birefringence observed in drawn coalesced and asr-PCL fibers. The improved mechanical properties of coalesced PCL fibers make them a better candidate for use in tissue engineering as scaffolds.
In this study, optically transparent glass fiber-reinforced polymers (tGFRPs) were produced using a thermoset matrix and an E-glass fabric. In situ polymerization was combined with liquid composite molding (LCM) techniques both in a resin transfer molding (RTM) mold and a lite-RTM (L-RTM) setup between two glass plates. The RTM specimens were used for mechanical characterization while the L-RTM samples were used for transmittance measurements. Optimization in terms of the number of glass fabric layers, the overall degree of transparency of the composite, and the mechanical properties was carried out and allowed for the realization of high mechanical strength and high-transparency tGFRPs. An outstanding degree of infiltration was achieved maintaining up to 75% transmittance even when using 29 layers of E-glass fabric, corresponding to 50 v. % fiber, using an L-RTM setup. RTM specimens with 44 v. % fiber yielded a tensile strength of 435.2 ± 17.6 MPa, and an E-Modulus of 24.3 ± 0.7 GPa.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.