In this research, a novel cotton fiber with a silk fibroin (SF) coating was prepared by the oxidation of a cotton thread with sodium periodate and subsequent treatment in a solution of silk fibroin. The structures of both the oxidized cotton samples and the SF modified cotton samples were investigated by Fourier transform infrared (FT-IR) in combination with Xray photoelectron spectroscopy (XPS) analysis. Other performances such as surface morphology and breaking strength were also studied. The results indicated that the weight of the oxidized cotton samples increased during SF treatment, while that of the un-oxidized cotton (pure cotton) samples reduced after SF treatment. Compared with the pure cotton samples, the oxidized cotton clearly showed a characteristic absorption band at 1730 cm 1 due to the stretching vibration of the C=O double bond of the aldehyde group. After being treated with the SF solution, the oxidized cotton fiber showed a weakened characteristic absorption band at 1730 cm 1 and a new absorption band at round 1540 cm 1 , suggesting the formation of C-N bond between aldehyde groups in the oxidized cotton and primary amines in the silk fibroin. The results were also confirmed by XPS analysis. Compared with the oxidized cotton samples, the SF treated cottons had relatively smooth surfaces, similar breaking strength, and the improved wrinkle recovery angles. The results in this research suggest that cotton based materials with protein coating can be achieved without using any other crosslinking agents by the method introduced.

An amino-terminated hyperbranched polymer (HBP-NH 2 ), synthesized from methyl acrylate and diethylene triamine by polycondensation, was applied to treat cotton samples by a pad-dry-cure method. Physical properties, salt-free dyeability, antimicrobial activity, and antiultraviolet property of the treated cotton samples were tested. The crystallinity and mechanical properties, including breaking strength, breaking elongation, and Young's modulus of the treated cotton fibers, increased slightly in comparison with those of the untreated cotton fibers. The thermal stability and the moisture regain were also improved slightly. Dyed with direct dyes and reactive dyes in the absence of the electrolytes, the treated cotton fabric showed similar or higher color strength compared with the untreated cotton fabric in conventional dyeing. The treated cotton fabric can also be dyed with acid dyes effectively. In addition, the treated cotton fabric showed good antimicrobial activities against Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli). The study of the antiultraviolet properties of the treated cotton fabric indicated that the HBP-NH 2 contributed to the reduction of UV transmission and the increase of UPF.