The diffusion of Ge in Ge-rich layer (GRL) and the factors affecting on it during the oxidation of strained Si1−xGex layers were examined. Strained Si1−xGex layers, having different initial Ge concentrations (x=0.15 and 0.3), were oxidized at 800 and 900°C in a dry O2 ambient for different oxidation times. The diffusion of Ge into the underlying Si1−xGex layer having an initial constant composition and the resulting transformation to GRL were both enhanced with an increase in oxidation temperature. After complete transformation to GRL, GeO2 started to become incorporated into the resulting oxide layer. The formation of GeO2 was initiated by the Ge saturation of the GRL layer with Ge and by the differences in diffusivity of Ge atoms in Si1−xGex and Si substrate. The relaxation occurred when the Ge concentration in the GRL reached a critical value and was not affected by either oxidation time or temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.