In this research, keratin was extracted from the disposable chicken feather using l-cysteine as reducing agent. Then, it was re-dissolved in the sodium carbonate-sodium bicarbonate buffer, and the pure keratin membrane and fiber were fabricated by doctor-blade casting process and wet spinning method, respectively. Scanning electron microscopy (SEM), fourier transform infrared (FT-IR) spectroscopy, X-ray diffraction (XRD) and thermogravimetric analysis (TGA) were used to characterize the chemical and physical properties of resulting powder, membrane and fiber. Compared with the raw chicken feather, the regenerated keratin materials retain its chemical structure and thermal stability, their relative crystallinity is a little different depend on the shaping method, which leads to the difference in moisture regain. The mechanical results show that tensile strength of the keratin membrane researches 3.5MPa, have potential application in biomedical fields. However, the keratin fiber presents low tenacity, i.e. 0.5cN/dtex, this problem should be solved in order to apply the new fiber in textile and material science.

In the present study, regenerated cellulose membrane with "imprinted morphology" and low crystallinity was fabricated from the crystal cellulose/[Bmim]Cl solution. Spherulites of 1-butyl-3-methilimidazolium chloride ([Bmim]Cl) and cellulose/ [Bmim]Cl solution were observed using polarized optical microscopy under certain condition. The fabricated cellulose membranes presented some particular characteristics compared with the membrane prepared from traditional cellulose/[Bmim]Cl solution. All the fabricated membranes were characterized by optical microscope, Wide-angle X-ray diffraction (WAXD), thermo-gravimetric analysis, and mechanical testing. The images showed that the resulting membranes prepared from crystal cellulose/[Bmim]Cl solution were "imprinted" with patterns which originated from the crystalline structure of [Bmim]Cl. The results of WAXD showed that the obtained cellulose membrane exhibited low diffraction peaks and crystallinity of approximately 24.57%. Furthermore, the low crystallinity led to the low mechanical property (27.5 MPa), thermal stability (315.4 8C), and high moisture regain (9.5%). V C 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43798.

Keratin particles with microscale are prepared by ball mill and its influences on the chitosan membrane is evaluated. Composite membranes with various content of keratin are fabricated, and their physical and chemical properties such as morphology, wettability, crystallization, thermal stability, tensile strength, and break elongation are investigated. Optical microscope and situ topographic scan mode of nano‐test system are used to examine the dispersion and aggregation of keratin on the surface of chitosan membrane. The result of contact angle (CA) and mechanical testing show that the incorporation of keratin particles decrease the CA from 98.1° to 58.2°. Tensile strength and break elongation of the composite membrane reaches a maximum of 65 ± 8 MPa and 15% when the keratin content is 6%, an increase of 80% and 88% compared with the pristine chitosan membrane. Both the increase in tensile strength and break elongation is result of the incorporation of keratin particles known for their excellent compatibility between keratin and chitosan matrix. These kind of composite material combines the antibacterial properties of chitosan with cell culture preference of keratin which may have potential biomedical application. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 44667.

CdS has attracted much attention due to its suitable bandgap and excellent photocatalytic performance for producing renewable H2 energy. However, photogenerated holes in CdS moves slowly relative to photogenerated electrons,...