An absorbent hydrogel with high-permeable solution resistance was prepared by free radical polymerization and crosslinking, by the process of micro/nano cellulose grafting with acrylic acid (AA) and 2-acrylamide-2-methyl propyl sulfonic acid (AMPS). Imbibition swelling curves revealed that absorbency of the hydrogel reached 70.2, 483.9, and 436.7 g/g in 0.9 wt% sodium chloride solution, 3 wt% urea solution, and rainwater, respectively. Fourier transform infrared results confirmed that acrylic acid (AA) and 2-acrylamide-2-methyl propyl sulfonic acid (AMPS) were grafted onto the micro/nano cellulose surface and the fiber structure persisted. Analysis with a confocal laser scanning microscope showed many pores on the polymer’s surface. Roughness became larger after grafting, which was conducive to water absorption capacity. Scanning electron microscopy (SEM) results showed that the main morphology of micro/nano cellulose did not change. BET results showed the presence of mesopores and macropores, which made the absorbent hydrogel highly permeable, allowing the internal and external absorbent groups to absorb water. H NMR confirmed that the cellulose was grafted with water-absorbent groups. In addition, lamellar structure and porous network morphology showed graft reaction occurred on the surface of micro/nano cellulose. The hydrogel has potential for agriculture and forestry, including in desertified and self-irrigated areas.
Poplar and pine wood were extracted with water, 1% NaOH (wt%) solution, and benzene:ethanol solution (V1 : V2, 2 : 1) to investigate the governing factors and mechanism by which extractives affect wood structure and mechanical properties. The structure, pore distribution, crystal structure, and mechanical properties of samples were analyzed by Fourier transform infrared spectroscopy (FTIR), adsorption of N2 gas, X-ray diffraction (XRD), and mechanical testing, respectively. The results demonstrated that cellulose, hemicellulose, and lignin were degraded to some extent in the course of the dissolution of the extractives. This degradation had a great influence on the structure and quantity of pores. The extraction treatment did not change the crystallization type of the wood, but it increased the crystallinity of the wood, and the length and width of the crystallization area changed. In addition, the mechanical properties of wood were changed when the content of the extractives was reduced.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.