We report an operando examination of a model nanocrystalline In2O3 catalyst for methanol synthesis via CO2 hydrogenation (300 °C, 20 bar) by combining X-ray absorption spectroscopy (XAS), X-ray powder diffraction (XRD), and in situ transmission electron microscopy (TEM). Three distinct catalytic regimes are identified during CO2 hydrogenation: activation, stable performance, and deactivation. The structural evolution of In2O3 nanoparticles (NPs) with time on stream (TOS) followed by XANES-EXAFS-XRD associates the activation stage with a minor decrease of the In–O coordination number and a partial reduction of In2O3 due to the formation of oxygen vacancy sites (i.e., In2O3–x ). As the reaction proceeds, a reductive amorphization of In2O3 NPs takes place, characterized by decreasing In–O and In–In coordination numbers and intensities of the In2O3 Bragg peaks. A multivariate analysis of the XANES data confirms the formation of In2O3–x and, with TOS, metallic In. Notably, the appearance of molten In0 coincides with the onset of catalyst deactivation. This phase transition is also visualized by in situ TEM, acquired under reactive conditions at 800 mbar pressure. In situ TEM revealed an electron beam assisted transformation of In2O3 nanoparticles into a dynamic structure in which crystalline and amorphous phases coexist and continuously interconvert. The regeneration of the deactivated In0/In2O3–x catalyst by reoxidation was critically assessed revealing that the spent catalyst can be reoxidized only partially in a CO2 atmosphere or air yielding an average crystallite size of the resultant In2O3 that is approximately an order of magnitude larger than the initial one.
Heterogeneous catalysts play a pivotal role in the chemical industry. The strong metalsupport interaction (SMSI), which affects the catalytic activity, is a phenomenon researched for decades. However, detailed mechanistic understanding on real catalytic systems is lacking. Here, this surface phenomenon was studied on an actual platinum-titania catalyst by state-of-the-art in situ electron microscopy, in situ X-ray photoemission spectroscopy and in situ X-ray diffraction, aided by density functional theory calculations, providing a novel real time view on how the phenomenon occurs. The migration of reduced titanium oxide, limited in thickness, and the formation of an alloy are competing mechanisms during high temperature reduction. Subsequent exposure to oxygen segregates the titanium from the alloy, and a thicker titania overlayer forms. This role of oxygen in the formation process and stabilization of the overlayer was not recognized before. It provides new application potential in catalysis and materials science.
Single-atom catalysts (SACs) have emerged as one of the most promising alternatives to noble metal-based catalysts for highly efficient oxygen reduction reaction (ORR). While SACs can offer notable benefits in terms of lowering overall catalyst cost, there is still room for improvement regarding catalyst activity. To this end, we designed and successfully fabricated an ORR electrocatalyst in which atomic clusters are embedded in an atomically dispersed Fe–N–C matrix (FeAC@FeSA–N–C), as shown by comprehensive measurements using aberration-corrected scanning transmission electron microscopy (AC-STEM) and X-ray absorption spectroscopy (XAS). The half-wave potential of FeAC@FeSA–N–C is 0.912 V (versus reversible hydrogen electrode (RHE)), exceeding that of commercial Pt/C (0.897 V), FeSA–N–C (0.844 V), as well as the half-wave potentials of most reported non-platinum-group metal catalysts. The ORR activity of the designed catalyst stems from single-atom active centers but is markedly enhanced by the presence of Fe nanoclusters, as confirmed by both experimental measurements and theoretical calculations.
The dynamic interactions between noble metal particles and reducible metal-oxide supports can depend on redox reactions with ambient gases. Transmission electron microscopy revealed that the strong metal-support interaction (SMSI)–induced encapsulation of platinum particles on titania observed under reducing conditions is lost once the system is exposed to a redox-reactive environment containing oxygen and hydrogen at a total pressure of ~1 bar. Destabilization of the metal–oxide interface and redox-mediated reconstructions of titania lead to particle dynamics and directed particle migration that depend on nanoparticle orientation. A static encapsulated SMSI state was reestablished when switching back to purely oxidizing conditions. This work highlights the difference between reactive and nonreactive states and demonstrates that manifestations of the metal-support interaction strongly depend on the chemical environment.
Light elements in the interstitial site of transition metals have strong influence on heterogeneous catalysis via either expression of surface structures or even direct participation into reaction. Interstitial atoms are generally metastable with a strong environmental dependence, setting up giant challenges in controlling of heterogeneous catalysis. Herein, we show that the desired carbon atoms can be manipulated within nickel (Ni) lattice for improving the selectivity in acetylene hydrogenation reaction. The radius of octahedral space of Ni is expanded from 0.517 to 0.524 Å via formation of Ni 3 Zn, affording the dissociated carbon atoms to readily dissolve and diffuse at mild temperatures. Such incorporated carbon atoms coordinate with the surrounding Ni atoms for generation of Ni 3 ZnC 0.7 and thereof inhibit the formation of subsurface hydrogen structures. Thus, the selectivity and stability are dramatically improved, as it enables suppressing the pathway of ethylene hydrogenation and restraining the accumulation of carbonaceous species on surface.
Carbon deposition following thermal methane decomposition under dry and steam reforming conditions has been studied on yttria-stabilized zirconia (YSZ), Y2O3, and ZrO2 by a range of different chemical, structural, and spectroscopic characterization techniques, including aberration-corrected electron microscopy, Raman spectroscopy, electric impedance spectroscopy, and volumetric adsorption techniques. Concordantly, all experimental techniques reveal the formation of a conducting layer of disordered nanocrystalline graphite covering the individual grains of the respective pure oxides after treatment in dry methane at temperatures T ≥ 1000 K. In addition, treatment under moist methane conditions causes additional formation of carbon-nanotube-like architectures by partial detachment of the graphite layers. All experiments show that during carbon growth, no substantial reduction of any of the oxides takes place. Our results, therefore, indicate that these pure oxides can act as efficient nonmetallic substrates for methane-induced growth of different carbon species with potentially important implications regarding their use in solid oxide fuel cells. Moreover, by comparing the three oxides, we could elucidate differences in the methane reactivities of the respective SOFC-relevant purely oxidic surfaces under typical SOFC operation conditions without the presence of metallic constituents.
Hetero-epitaxial growth along three-dimensional (3D) interfaces from materials with an intrinsic large lattice mismatch is a key challenge today. In this work we report, for the first time, the controlled synthesis of vertically aligned ZnO/ZnS core/shell nanorod arrays composed of single crystalline wurtzite (WZ) ZnS conformally grown on ZnO rods along 3D interfaces through a simple two-step thermal evaporation method. Structural characterization reveals a "(01-10)(ZnO)//(01-10)(ZnS) and [0001](ZnO)//[0001](ZnS)" epitaxial relationship between the ZnO core and the ZnS shell. It is exciting that arrays of single crystalline hollow ZnS nanotubes are also innovatively obtained by simply etching away the inner ZnO cores. On the basis of systematic structural analysis, a rational growth mechanism for the formation of hetero-epitaxial core/shell nanorods is proposed. Optical properties are also investigated via cathodoluminescence and photoluminescence measurements. Remarkably, the synthesized ZnO/ZnS core/shell heterostructures exhibit a greatly reduced ultraviolet emission and dramatically enhanced green emission compared to the pure ZnO nanorods. The present single-crystalline heterostructure and hollow nanotube arrays are envisaged to be highly promising for applications in novel nanoscale optoelectronic devices, such as UV-A photodetectors, lasers, solar cells, and nanogenerators.
Gold nanoparticles on transition-metal oxides were synthesized by two different methods: precipitation and photoinduced decomposition of an intermediate gold–azido complex. Only samples prepared by the precipitation method showed significant CO conversion at low temperature. XPS shows the formation of two Au species (Au0 and Auδ+) on the surface of active Au/TiO2 and Au/Fe2O3 samples. The energy shift of the Auδ+ peak depends on the support and is 0.6 and 0.9 eV for Au/TiO2 and Au/Fe2O3, respectively. TEM images indicate the formation of overlayer on Au particles. These results prove Au activation via a strong metal–support interaction, on the basis of the strong influence of the support on the electronic structure of the gold through charge transfer and stabilization of low-coordinated Au atoms.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.