Polyurea is a synthetic material made by the reaction of isocyanate and polymer blend-containing amines. Due to its outstanding mechanical properties and fast curing, polyurea-based coatings have found dozens of applications, including waterproofing and anti-corrosion coatings. Further development of this material can create a flame-retardant product, a good alternative for common products available on the market, such as intumescent coatings. To improve the flame retardancy of polyurea, several flame retardants were investigated. The influence of aluminum hydroxide, resorcinol bis(diphenyl phosphate) (RDP), and tris chloropropyl phosphate (TCPP) on flame retardancy and morphology was studied. The following methods were used: infrared spectroscopy, scanning electron microscopy, thermogravimetric analysis, limiting oxygen index, and tensile strength. The examinations mentioned above showed the improvement of flame-retardancy of polyurea for two products: chlorinated organophosphate and organophosphate. Nevertheless, using the chlorinated organophosphate additive caused a rapid deterioration of mechanical properties.
This paper presents the results of tests on elastomer coatings based on polyurea–polyurethane formulation with increased fire parameters. Coatings modified with flame retardants: bis(phenylphosphate) resorcinol (RDP), trischloropropyl phosphate (TCPP), and aluminum hydroxide (ATH) were tested. Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA/DTG) were used to investigate the structure and thermal stability. The effectiveness of resorcinol bis(phenylphosphate) (RDP), tris chloropropyl phosphate (TCPP), and aluminum hydroxide (ATH) on heat release rate (HRR), smoke release rate (RSR), and oxygen consumption was evaluated using cone calorimetry. The cone calorimetry results were correlated with the mechanical properties of the coatings. The cone calorimetry analysis showed suitable organophosphorus flame retardant (FR) performance, significantly decreasing HRR and oxygen consumption. Additionally, 15% TCPP caused a reduction of HRR by over 50%, obtaining 211.4 kW/m2 and pHRR by over 55%, reaching 538.3 kW/m2. However, organophosphorus flame retardants caused a significant deterioration of mechanical properties simultaneously. Introducing a mixture of two FRs (RDP/TCPP) resulted in obtaining a coating with improved fire resistance and maintained good mechanical strength. The polyurea–polyurethane coating, modified with a mixture of two RDP/TCPP retardants (10:5), was simulated for the burning of roof systems. The result of the simulation was assessed positively. Thus, finally, it was confirmed that the proposed polyurea–polyurethane coating achieved the assumed flame retardant level.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.