Annealing Pb(Zr 1Àx Ti x )O 3 (PZT) thin films in the hydrogen ambient can result in the unacceptable degradation of ferroelectric properties due to interaction of H 2 forming gas with the ferroelectric materials. Since the understanding of this degradation mechanism is limited, this issue arouses a big problem for the application of PZT in high-density non-volatile ferroelectric random access memories (NVFRAM). In order to resolve this problem, we investigate Pt/PZT/Pt capacitors before and after H 2 annealing at various temperatures. The capacitors lost their ferroelectric properties during hydrogen annealing. The measurements of polarization hysteresis loops and leakage currents suggest that there are different degradation mechanisms for the reduced PZT films. Although hydrogen induced degradation can be partially recovered by postannealing of the thin films in the O 2 ambient, all the remanent polarizations after recovery are much smaller than their virgin values, which indicates the irreversible damage of the ferroelectricity during the forming gas annealing (FGA) process. In order to investigate the degradation mechanism, X-ray diffraction was performed before and after FGA, and atomic force microscopy images were taken to observe the topograghy and microstructure changes. A conductive Pt-coated piezoelectric force microscope probe was used as a mobile top electrode to check ferroelectric and piezoelectric properties within microregions of PZT films before and after FGA.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.