Silver‐loading asymmetric cellulose acetate (CA) hollow fiber membrane was spun via the dry jet‐wet spinning technique. The spinning solution was prepared by dissolving AgNO3 and CA in N,N‐dimethylformamide (DMF). The silver ions were reduced in the spinning dope into silver nano‐particles. The morphology of the resulting hollow fibers was examined using a scanning electron microscope and the silver content in the fiber was measured using an inductively coupled plasma atomic emission spectrometer. The antibacterial activities were evaluated. These hollow fibers had a sponge‐like structure and dense inner and outer surfaces. At a 50 k magnification, the pore on the skin layer was not observable, while the nodule size was smaller than 10 nm. The residual silver content of as‐spun hollow fiber was about 60% of the original silver added in the polymer solution. After immersing in water bath for 180 days, the silver content in the bulk of the hollow fibers decreased to 60% and the silver content on the surface reduced to 10%, yet still showed antibacterial activity against Escherichia coli and Staphylococcus aureus. After permeating with water for 5 days, the silver content in the hollow fibers decreased, and did not show antibacterial activity against E. coli and S. aureus. Thus, silver content must be periodically replenished after permeation. The proper range of AgNO3 in the spinning solution for CA hollow fiber should be about 100–1000 ppm. Copyright © 2005 John Wiley & Sons, Ltd.

No abstract

No abstract

Poly(ethylene terephthalate) (PET) fibers were treated with 60 Co-g-ray and grafted with acrylic acid. The resulting fibers were further grafted with chitosan (CS) via esterification. Afterward, hyaluronic acid (HA) was immobilized onto CS-grafting fibers. The antibacterial activity of CS against S. aureus, E. coli, and P. aeruginosa was preserved after HA-immobilization. After immobilizing HA, the L929 fibroblasts cell proliferation was improved for CS-grafting PET fiber. The results indicate that by grafting with CS and immobilizing with HA, PET fibers not only exhibit antibacterial activity, but also improve the cell proliferation for fibroblast.

No abstract