Polymer nanogels are used as colloidal stabilisers in emulsion polymerization. The nanogels were made by the covalent crosslinking of block copolymer micelles, the macromolecular building blocks of which were synthesized using a combination of catalytic chain transfer emulsion polymerization and reversible addition fragmentation chain-transfer (RAFT) of methacrylate monomers. The use of the nanogels in an emulsion polymerization led to anisotropic Janus and patchy colloids, where a latex particle was decorated by a number of patches on its surface. Control on the particle size and patch density was achieved by tailoring of the reaction conditions, such as varying the amount of nanogels, pH and salt concentration. Overall, the emulsion polymerization process in the presence of nanogels as stabilizers is shown to be a versatile and easily scalable route towards the fabrication of Janus and patchy polymer colloids.

This study used Raman spectro-microscopy to investigate the synthesis and degradation of radiation-grafted anion-exchange membranes (RG-AEM) made using 50 μm thick poly(ethylene-co-tetrafluoroethylene) (ETFE) films, vinylbenzyl chloride (VBC) monomer, and 1-methylpyrrolidine (MPY) amination agent. The data obtained confirmed the operation of the grafting-front mechanism. VBC grafting times of 1 and 4 h led to low degrees of grafting homogeneity, while 72 h led to extreme levels of grafting that resulted in mechanically weak RG-AEMs due to the excessive H2O contents. A grafting time of 16 h was optimal yielding a RG-AEM with an ion-exchange capacity (IEC) of 2.06 ± 0.02 mmol g-1 (n = 3). An excess of grafting was detected at the surface of this RG-AEM (at least within the first few μm of the surface). This RG-AEM was then degraded in O2-purged aqueous KOH (1.0 mol dm-3) for 14 d at 80 °C. Degradation was detected throughout the RG-AEM cross-section, where the Raman data was quantitatively consistent with the loss of IEC. A slight excess of degradation was detected at the surface of the RG-AEM. Degradation involved the loss of whole benzyl-1-methypyrrolidinium grafted units as well as the direct attack on the pendent (cationic) pyrrolidinium groups by the hydroxide anions