Fine magnetic particles (sizeffi100 Å ) belonging to the series Zn x Fe 1Àx Fe 2 O 4 were synthesized by cold co-precipitation methods and their structural properties were evaluated using X-ray diffraction. Magnetization studies have been carried out using vibrating sample magnetometry (VSM) showing near-zero loss loop characteristics. Ferrofluids were then prepared employing these fine magnetic powders using oleic acid as surfactant and kerosene as carrier liquid by modifying the usually reported synthesis technique in order to induce anisotropy and enhance the magneto-optical signals. Liquid thin films of these fluids were prepared and field-induced laser transmission through these films was studied. The transmitted light intensity decreases at the centre with applied magnetic field in a linear fashion when subjected to low magnetic fields and saturate at higher fields. This is in accordance with the saturation in cluster formation. The pattern exhibited by these films in the presence of different magnetic fields was observed with the help of a CCD camera and was recorded photographically. r
Ferrofluids belonging to the series, Ni x Fe 1−x Fe 2 O 4 and Zn x Fe 1−x Fe 2 O 4 , were synthesized using cold co-precipitation. Liquid films of these ferrofluids were prepared by encapsulating the ferrofluids in between two optically smooth and ultrasonically cleaned glass plates. Magnetic field induced laser transmission through these ferrofluid films has been investigated. Magnetic field values can be calibrated in terms of output laser power in the low field region in which the variation is linear. This set up can be used as a cheap optical gaussmeter in the low field regime. Using the same set-up, the saturation magnetization of the sample used can also be calculated with a sample that is pre-characterized. Hence both magnetization of the sample, as well as applied magnetic field can be sensed and calculated with a precalibrated sample.
Ultra fine precursors for ferrofluid synthesis, belonging to the series, Ni x Fe 1-x Fe 2 O 4 (where 'x' varies from '0' to '0⋅ ⋅6' in steps of 0⋅ ⋅1), were synthesized. Ferrofluids based on these fine particles were prepared with oleic acid as surfactant and kerosene as carrier. Ferrofluidic thin films were made on glass substrates and magnetic field induced laser transmission was studied. The pattern exhibited by the films under the influence of a magnetic field was observed with the help of a CCD camera. The analysis of results confirms the chain formation of particles in the presence of an applied magnetic field and their saturation at higher applied fields. Keywords. Ferrofluids; nickel ferrite; field induced assembling; ultra fine particles.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.