The characterization of the microstructure, morphology, topography, composition, and physical and chemical properties of the coatings containing β-tricalcium phosphate (β-TCP) particles deposited by the micro-arc oxidation (MAO) method on biodegradable Mg-0.8Ca alloy has been performed. The electrolyte for the MAO process included the following components: Na 2 HPO 4 •12H 2 O, NaOH, NaF, and β-Ca 3 (PO 4) 2 (β-TCP). The coating morphology, microstructure, and compositions have been studied using scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX), and X-ray diffraction (XRD). With increasing of the MAO voltage from 350 to 500 V, the coating thickness and surface average roughness of the coatings increased linearly from 6 to 150 µm and from 2 to 8 µm, respectively. The coating deposited at 350 V had more homogeneous porous morphology with numerous pores similar by sizes (2-3 µm) than the coatings formed at 450-500 V. The β-TCP isometric particles were included in the coating surface. The XRD recognized the amorphous-crystalline structure in the coatings with incorporation of the following phases: β-TCP, α-TCP, MgO (periclase) and hydroxyapatite (HA). The corrosion experiments showed that the biodegradation rate of the Mg-0.8Ca alloy coated by calcium phosphates is almost 10 times less than that of uncoated alloy.

This work consists of two parts. In the first part, the kinetics and mechanism of corrosion on the surface of the welded joint area of the aircraft 1579 aluminium alloy have been studied using SVET (scanning vibrating electrode technique) and SIET (scanning ion-selective electrode technique) in 0.5 M NaCl. The results have revealed the corrosion process development within the weld interface due to the presence of microdefects in the morphological structure. Features of the 1579 Al alloy corrosion have also been investigated through immersion experiments, quantitative analysis of dissolved alloying elements by means of atomic absorption spectroscopy, and corrosion products characterization using XRD (X-ray diffraction) analysis. The presence of Mg as an alloying element in the 1579 Al alloy sufficiently increases the bulk pH values as a result of the intensive dissolution of Mg. These factors accelerate the corrosion activity of the studied material in the 0.5 M NaCl solution. Corrosion evolution analysis of the 1579 Al alloy sample showed the importance of the coating formation to protect this alloy against corrosion and to increase the stability of this system in the corrosive media.

No abstract

No abstract