ABSTRACT:The objective of this study was to evaluate the accuracy of nondestructive variables in inferring basic density of wood from Eucalyptus grandis and Eucalyptus urophylla. A total of 27 clones of Eucalyptus urophylla and 22 clones of Eucalyptus grandis were used, sourced from a clonal trial set up in Martinho Campos, Minas Gerais. After evaluation using nondestructive techniques of resistography and pin penetration at a constant pressure (Pilodyn ® ), individuals were felled and disks were removed from the 2%, 10%, 30%, 50% and 70% portions of the merchantable height section, and also from the portion 1.30 m above ground level. Basic density was determined by the water immersion method. Values of basic density ranged from 0.412 to 0.609 g.cm -3 for clones at age 42 months and from 0.408 to 0.664 g.cm -3 for clones at age 54 months. The clones of Eucalyptus urophylla provided higher values of average basic density in relation to Eucalyptus grandis. The variable 'amplitude' had better correlation with basic density in comparison with pin penetration at a constant pressure. Nondestructive evaluation can be used in mass preselection of genetic materials, prior to subjecting them to a more accurate, reliable evaluation.
This research aimed to select Eucalyptus clones for bioenergy production by using of two multivariate techniques, principal component analysis and cluster analysis. The analysis evaluated 25 clones of Eucalyptus at age 54 months. Determinations included the concentrations of elemental components (C, H and O), lignin, total extractives and ash, as well as basic density, higher heating value and energy density. Both multivariate methods being used to evaluate and select clones of Eucalyptus for bioenergy production proved effective, there being similarities between the biomass groups formed by them. The cluster analysis revealed five distinct groupings, out of which cluster one, formed by clone U060, was found to have greater potential as a source of energy. Clones G084, G122, G023 and U108 had poorer energy performance.
RESUMO:Neste trabalho, objetivou-se avaliar o desempenho físico-mecânico de painéis de lâminas paralelas (LVL) produzidos com diferentes composições de espécies tropicais amazônicas e Pinus oocarpa. Foram utilizadas três espécies tropicais: Cordia goeldiana Huber. (Freijó), Parkia gigantocarpa Ducke (Faveira) e Brosimum parinarioides Ducke (Amapá doce). Para comparação, foi utilizada madeira de Pinus oocarpa proveniente de plantio experimental. Três tipos de combinações de lâminas foram avaliados: (i) uma espécie, (ii) combinação das três espécies amazônicas e (iii) combinação de espécies amazônicas com Pinus oocarpa. Avaliouse também a velocidade de propagação acústica com o stress wave timer para a determinação do módulo de elasticidade dinâmico (MOEd), que foi correlacionado com o módulo de elasticidade estático (MOEe) do painel. Os painéis produzidos com espécies da Amazônia apresentaram menor absorção de água total em relação aos painéis de Pinus oocarpa. Para as propriedades mecânicas, a menor resistência foi verificada para painéis de faveira. Não houve diferença estatística entre os painéis para a resistência ao cisalhamento na linha de cola. O stress wave timer poderia ser utilizado para predição do MOEe a partir do MOEd.Palavras-chave: Painel estrutural, stress wave timer, madeiras tropicais. MECHANICAL AND PHYSICAL PROPERTIES OF LVL PANELS MADE FROM THREE AMAZONIC SPECIES ABSTRACT: This work aimed to evaluate the physical-mechanical performance of laminated veneer lumber (LV) produced with different compositions of tropical Amazonian species and Pinus oocarpa. Three tropical species were used: Cordia goeldiana Huber. (Freijó), Parkia gigantocarpa Ducke (Faveira) and Brosimum parinarioides Ducke (Amapá doce). For comparison, Pinus oocarpa wood obtained from an experimental stand was used. Three types of veneer combination were evaluated: (i) one species; (ii) the three Amazonian species combination and (iii) combination of Amazonian species with
This work aimed to investigate the feasibility of using and mixing Toona ciliata, Eucalyptus grandis/ urophylla and Pinus oocarpa woods in OSB production. Three one-species and four mixed-species combinations were compared. Layer structure varied by positioning different wood species in the surface and core of the panels. Phenol-formaldehyde (PF) adhesive was applied at 9% for all OSB panels. Three-layer mats with mass proportion of 25/50/25% for surface/core/surface were produced. Pressing time was 8 min, under a 4 MPa pressure and temperature of 180 ˚C. Physical and mechanical properties were evaluated and compared to EN (300) commercialization standard. Most OSB panels did not fully attain such requirements. OSB panels made with Eucalyptus grandis/urophylla and Pinus oocarpa woods have potential to be commercialized as OSB/1 and OSB/2 types, respectively. Among panels made with T. ciliata wood, those produced with this species in the surface and Eucalyptus grandis/urophylla wood in the core met the requirements established for OSB/1 commercialization. Eucalyptus wood has great potential to substitute Pinus wood in OSB production. The utilization of T. ciliata wood for OSB production decreased mechanical performance, but remarkably enhanced water resistance properties.
Objetivou-se, com o presente trabalho, avaliar as propriedades físicas e mecânicas de painéis compensados produzidos a partir de madeira de Toona ciliata com duas pressões e duas gramaturas distintas, além da influência da inclusão de lâminas de Pinus sp. na qualidade desses painéis. Foram produzidos compensados de cinco lâminas com resina fenol-formaldeído. Os ensaios físico-mecânicos foram realizados de acordo com as especificações descritas na norma ABNT 31:000.05-001/2(2001). Os resultados de densidade aparente, absorção de água após 24 horas, flexão estática (MOR e MOE) e resistência ao cisalhamento seco na linha de cola apresentaram diferenças significativas entre os tratamentos. Todos os tratamentos apresentaram valor de MOE e MOR paralelo acima do exigido pela norma NBR 31.000.001/2:2001, no entanto apenas os painéis com inclusão de Pinus sp. no miolo atingiram MOE e MOR perpendicular acima do estipulado pela mesma. Para os ensaios de resistência de colagem ao esforço do cisalhamento, os painéis apresentaram valores superiores ao mínimo exigido pela norma EN 314-2 (1993). Comparando-se os painéis produzidos somente com Toona ciliata, não foi observada influência da gramatura de cola e da pressão sobre nenhuma das propriedades físicas e mecânicas avaliadas. A inclusão de lâminas de Pinus sp. tanto nas camadas internas quanto nas camadas externas dos painéis contribuiu para melhorar a maioria das propriedades físicas e mecânicas.
O objetivo deste trabalho foi avaliar a influência da razão de compactação sobre propriedades físicas e mecânicas de painéis aglomerados por meio de modelos lineares simples. Foram produzidos painéis em três composições distintas: 1) 100% Toona ciliata; 2) 50% Toona ciliata + 50% Pinus sp.; 3) 50% Toona ciliata + 50% Eucalyptus sp. Para os modelos ajustados, foram realizadas análises de variância e teste de falta de ajuste. Os modelos foram avaliados de acordo com a significância de seus coeficientes, erro padrão da estimativa e coeficiente de determinação. A correlação linear de Pearson entre as variáveis foi determinada. Os módulos de elasticidade e ruptura aumentaram com o aumento da razão de compactação, tendo o contrário ocorrido para ligação interna, inchamento em espessura após 2 horas e absorção de água. Com exceção da compressão paralela às faces e inchamento em espessura, foram obtidos bons ajustes de modelos para as demais variáveis.
RESUMO -Este trabalho teve por objetivo avaliar a viabilidade técnica de produção de painéis cimentomadeira compostos por diferentes proporções de resíduos das madeiras de cedro-australiano (Toona ciliata M. Roem.), Pinus taeda e clone de híbrido de Eucalyptus grandis x Eucalyptus urophylla, utilizando-se dois processos distintos de cura: vaporização e climatização. Foi utilizado o cimento Portland CP V -ARI/Plus como aglomerante e o cloreto de cálcio como aditivo químico. As partículas de madeira foram previamente tratadas em água fria durante 24 h. Foram considerados os seguintes parâmetros: relação madeira/cimento -1/2,75; relação água/cimento -1/2,5 (base peso do cimento); taxa de água de hidratação/cimento -25% (base peso do cimento); aditivo químico -4% (base peso do cimento); densidade nominal -1,10 g/cm 3 ; e dimensões dos painéis -480 x 480 x 150 mm. Os parâmetros de prensagem foram: temperatura ambiente, pressão específica de 40 kgf/cm² e tempo de 10 min. O tempo de grampeamento foi de 24 h. As propriedades avaliadas foram absorção de água e inchamento em espessura após 24 h, flexão estática, compressão e ligação interna. O experimento foi instalado segundo um delineamento inteiramente casualizado com três repetições e seis tratamentos, arranjados num esquema fatorial de três composições x dois processos de cura. Os painéis compostos pela mistura de T. ciliata com o clone de Eucalyptus apresentaram valores médios superiores para inchamento em espessura e resultados inferiores para a maioria das propriedades mecânicas. A cura a vapor melhorou as propriedades físicas, mas afetou negativamente a maioria das propriedades mecânicas.Palavras-chave: Cedro-australiano, Cura e Resíduos. MIXTURE OF THREE REFORESTATION SPECIES ON THE CEMENT-WOOD PANELS PRODUCTION
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.