Assessing the reliability of non-destructive testing (NDT) techniques in detecting in-service fatigue cracks is vital for ensuring the structural integrity of aero engines. However, the requirement of a large number of in-service failed components with numerous initiating fatigue cracks
makes it a cost-intensive methodology. Hence, laboratory samples with electrical discharge machined (EDM) notches representing fatigue cracks have also been used for NDT reliability studies. However, probability of detection (POD), a measure of NDT reliability, is usually a function of all
crack dimensions rather than only length. This limits the applicability of EDM notches (minimum width of notch ~0.3 mm) as artificial fatigue cracks for POD studies. The current study demonstrates the methodology of generating cracks under laboratory conditions in nickel-based superalloy samples
(representative aero engine material), mimicking in-service conditions such as crack tightness as low as 1 μm, crack tortuosity, transgranular nature, crack branching and multiple initiation sites of cracks. POD curves generated using these samples are demonstrated and the feasibility of
this approach is discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.