We report a low-temperature magneto transport study of Bi2Se3 thin films of different thicknesses (40, 80 and 160 nm), deposited on sapphire (0001) substrates, using radio frequency magnetron sputtering technique. The high-resolution x-ray diffraction measurements revealed the growth of rhombohedral c-axis {0003n} oriented Bi2Se3 films on sapphire (0001). Vibrational modes of Bi2Se3 thin films were obtained in the low wavenumber region using Raman spectroscopy. The surface roughness of sputtered Bi2Se3 thin films on sapphire (0001) substrates were obtained to be ~ 2.26–6.45 nm. The chemical and electronic state of the deposited Bi2Se3 was confirmed by X-ray photoelectron spectroscopy and it showed the formation of Bi2Se3 compound. Resistivity versus temperature measurements show the metallic nature of Bi2Se3 films and a slight up-turn transition in resistivity at lower temperatures < 25 K. The positive magneto-resistance value of Bi2Se3 films measured at low temperatures (2–100 K) confirmed the gapless topological surface states in Bi2Se3 thin films. The quantum correction to the magnetoconductivity of thin films in low magnetic field is done by employing Hikami–Larkin–Nagaoka theory and the calculated value of coefficient ‘α’ (defining number of conduction channels) was found to be 0.65, 0.83 and 1.56 for film thickness of 40, 80 and 160 nm, respectively. These observations indicate that the top and bottom surface states are coupled with the bulk states and the conduction mechanism in Bi2Se3 thin films varied with the film thicknesses.
To understand the spread of SARS-CoV2, in August and September 2020, the Council of Scientific and Industrial Research (India), conducted a sero-survey across its constituent laboratories and centers across India. Of 10,427 volunteers, 1058 (10.14%) tested positive for SARS CoV2 anti-nucleocapsid (anti-NC) antibodies; 95% of which had surrogate neutralization activity. Three-fourth of these recalled no symptoms. Repeat serology tests at 3 (n=607) and 6 (n=175) months showed stable anti-NC antibodies but declining neutralization activity. Local sero-positivity was higher in densely populated cities and was inversely correlated with a 30 day change in regional test positivity rates (TPR). Regional seropositivity above 10% was associated with declining TPR. Personal factors associated with higher odds of sero-positivity were high-exposure work (Odds Ratio, 95% CI, p value; 2∙23, 1∙92–2∙59, <0.0001), use of public transport (1∙79, 1∙43–2∙24, <0.0001), not smoking (1∙52, 1∙16–1∙99, 0∙0257), non-vegetarian diet (1∙67, 1∙41–1∙99, <0.0001), and B blood group (1∙36,1∙15-1∙61, 0∙001).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.