Chitosan microparticles were mixed with chitosan and carboxymethyl cellulose solution to achieve a good binding between the microparticles. Three different compositions of scaffolds were made by varying the calcium phosphate (CaP) amount: 0%, 10%, and 20%. Potassium chloride was used as salt, to make pores inside the scaffolds after leaching out when immersed in phosphate buffer saline (PBS). Compressive strength and compressive modulus of both non-porous (before leaching out), and porous (after leaching out) scaffolds were measured according to the ASTM standards. The highest compressive strength of 27 MPa was reported on 10% CaP scaffolds while 20% CaP scaffolds showed the lowest. The increasing CaP content reduces the compressive strength of the scaffolds. The highest wet state compressive strength was reported on 0% CaP scaffolds with 0.36 MPs and 0.40 MPa at day 1 and day 3 respectively. In vitro cell culture studies showed good cell adhesion and cell proliferation on 10% CaP scaffolds.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.