ABSTRACT. The modulus of elasticity of concrete is an important property because it is crucial for the control of deformation. The impossibility of obtaining concrete with higher elasticity modulus rates may cause economic liabilities due to the need for larger structural elements. Current paper evaluates three compressive strength classes (20, 30 and 40MPa) of concrete produced with two types of coarse aggregate, basalt and dolomite rock from the Triângulo Mineiro region, Brazil. Further, 459 cylindrical test specimens were cast for the experimental study. The experimental results of the elasticity modulus rates were compared and with formulations prescribed by four standards: ABNT NBR 6118, ACI 318, Eurocode 2 and FIB Model Code. Comparisons demonstrated that the effect of coarse aggregate on the elasticity modulus was negligible when compared to the concrete's resistance class.Keywords: deformation, properties, standards, experimental results.Influência do agregado graúdo no módulo de elasticidade do concreto RESUMO. O módulo de elasticidade do concreto é uma propriedade importante para os profissionais envolvidos na indústria da construção civil, uma vez que seu valor é determinante para o controle das deformações. A impossibilidade de se obter concretos de maior valor de módulo de elasticidade pode resultar em perda econômica pela necessidade de elementos estruturais de maior dimensão. Este trabalho avaliou o módulo de elasticidade de três classes distintas de concreto (C20, C30 e C40) produzidas com dois tipos morfológicos de rochas, basalto e dolomito, da região do Triângulo Mineiro. Como parte do estudo experimental, foram moldadas 459 amostras cilíndricas. Os valores de módulo de elasticidade obtidos foram comparados entre si e com formulações propostas em quatro normas: ABNT NBR 6118, ACI 318, Eurocode 2e FIB Model Code. Essas comparações indicaram que o efeito do tipo do agregado graúdo no módulo de elasticidade foi pouco expressivo quando comparado com a mudança da resistência do concreto.Palavras-chave: deformação, propriedades, normas, resultados experimentais.
Resumo O módulo de elasticidade do concreto é uma propriedade importante para os profissionais envolvidos na indústria da construção civil, uma vez que seu valor é determinante para o controle das deformações. Este trabalho avaliou o módulo de elasticidade de três classes distintas de concreto (C20, C30 e C40) produzidas com dois tipos litológicos de rochas, basalto e dolomito, de diferentes jazidas da região do Triângulo Mineiro. Como parte do estudo experimental, foram moldadas 324 amostras cilíndricas de 10 cm × 20 cm. Os valores de módulo de elasticidade obtidos foram comparados com seis formulações propostas em quatro normas, institutos e códigos do concreto: ABNT NBR 6118 versão 2007 e 2014, ACI 318, EUROCODE 2 and FIB Model Code, Ibracon 2003. Dentre as formulações propostas pelas normas, as indicadas pela FIB Model Code (2010) e ABNT NBR 6118 (2014) apresentaram valores mais próximos aos resultados experimentais deste estudo.
In this paper, an experimental investigation is presented on semi-rigid interior beam-to-column connections constituted by precast concrete beams supported on precast concrete column corbels and bending continuity reinforcement bars for bending negative moments. The main purpose of this paper was to analyze the influence of vertical interface grout filling between the corbel and the beam and the position of the bending continuity reinforcement bars (crossing only the column or crossing only the slab) on the behavior of this type of connection. Tests on eight specimens were performed. It was noticed that the vertical interface grout filling contributed to increase both rotational flexural stiffness and flexural strength capacity of the connections when compared to the connections without grout filling. It was also noticed that in the specimens in which the continuity bars crossed only the column, the rotational flexural stiffness was higher. For these last ones, coefficients k and β for predicting the secant stiffness by simplified expression present in Brazilian Code NBR 9062 were evaluate from experimental results. These evaluated coefficients may be regarded as indicative values for structural designers and helpful for future researches.
RESUMOO objetivo deste trabalho é apresentar o resultado da pesquisa sobre a influência que algumas variáveis exercem nos resultados dos ensaios de esclerometria e de velocidade do pulso ultrassônico (UPV), especificamente as seguintes variáveis: dimensão máxima característica dos agregados (DMA), a variação da umidade do concreto endurecido e da camada de concretagem nos resultados dos ensaios de esclerometria e de velocidade de pulso ultrassônico e a variação da distância entre os transdutores no ensaio de UPV. Os ensaios foram realizados em seis blocos de concreto com seis anos de idade e em dez vigas de concreto armado com dois anos. Nos blocos a relação água/cimento foi mantida e a DMA dos agregados foram 9,5 mm, 19,0 mm e 25,0 mm. Para as vigas foram mantidas todas as características. A variação da umidade no concreto foi obtida com a aspersão controlada de água. Pelos resultados de UPV concluiu-se que nos blocos com maior DMA, a UPV foi menor; a camada intermediária apresentou maior valor de UPV. Para blocos e vigas a UPV aumentou com o aumento do teor de umidade do concreto e diminui quando se aumentou a distância entre os transdutores. Foram obtidos os menores índices esclerométricos nos blocos contendo agregados com maior DMA. Para os blocos e vigas ocorreu um decréscimo do índice esclerométrico à medida que a umidade superficial aumentou. Palavras-chave: Ensaios não destrutivos, velocidade de pulso ultrassônico, esclerometria. ABSTRACTThe aim of this paper is to present the result of a study of the influence of some variables on the results of nondestructive testing of concrete, sclerometry (rebound hammer) and ultrasonic pulse velocity (UPV), specially in: Aggregates' size (DMA), concrete's moisture, casting concrete, and transducers' space. Moisture in concrete was obtained by controlled sprinkling water. The tests were conducted on six years old concrete blocks, and two years old reinforced concrete beams. Water/cement ratio of concrete blocks was maintained and DMA of coarse aggregates were 9.5 mm, 19.0 mm and 25.0 mm. The results of UPV revealed that blocks with the biggest DMA had lower UPV, the middle concrete layer presented bigger value of UPV than others. The UPV increased when the surface was sprinkled or the transducers space increased, for blocks and beams. The smaller rebound index was on blocks containing aggregates with the biggest DMA. For blocks and beams, the rebound index decreased when superficial moisture increased. Keywords: Nondestructive testing, ultrasonic pulse velocity, sclerometry (rebound hammer). -INTRODUÇÃOO concreto é um dos materiais mais utilizados no mundo e durante muito tempo foi considerado imutável ao longo do tempo. Somente na segunda metade do século XX foi verificado que o concreto tinha uma vida útil limitada a menos de um século. Tal constatação levou o meio científico e tecnológico a considerar aspectos de durabilidade nos projetos de estruturas de concreto armado. Apesar das recomendações das normas surtirem efeitos benéficos, as falhas acabam ocorrendo e...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.