Diamond-like carbon (DLC) films have been extensively applied in industries owing to their excellent characteristics such as high hardness. In particular, there is a growing demand for their use as protective films for mechanical parts owing to their excellent wear resistance and low friction coefficient. DLC films have been deposited by various methods and many deviate from the DLC regions present in the ternary diagrams proposed for sp3 covalent carbon, sp2 covalent carbon, and hydrogen. Consequently, redefining the DLC region on ternary diagrams using DLC coatings for mechanical and electrical components is urgently required. Therefore, we investigate the sp3 ratio, hydrogen content, and other properties of 74 types of amorphous carbon films and present the classification of amorphous carbon films, including DLC. We measured the sp3 ratios and hydrogen content using near-edge X-ray absorption fine structure and Rutherford backscattering-elastic recoil detection analysis under unified conditions. Amorphous carbon films were widely found with nonuniform distribution. The number of carbon atoms in the sp3 covalent carbon without bonding with hydrogen and the logarithm of the hydrogen content were inversely proportional. Further, we elucidated the DLC regions on the ternary diagram, classified the amorphous carbon films, and summarized the characteristics and applications of each type of DLC.
Polyimide (PI)-based composites containing single-wall carbon nanohorn aggregate (NH) were fabricated using the spark plasma sintering (SPS) process. For comparison, composites with carbon nanotube (NT) and traditional graphite (Gr) were also fabricated. The NH was produced using CO 2 laser vaporization and a graphite target and the NT was produced by a chemical synthesis method. We evaluated the friction and wear properties of the PI-based composites with a reciprocating friction tester in air using an AISI 304 mating ball. NH drastically decreased the wear of PI-based composites; the specific wear rate of composite with NH of only 5 wt% was of the order of 10 )8 mm 3 /Nm, which was two orders of magnitude less than that of PI alone. The wear reduction ability of NT seemed to be slightly inferior to that of NH, although it was considerably better than that of Gr. NH and NT lowered the friction of composites. The friction coefficient of composite with 10 wt% NH was less than 0.25, although it was slightly higher than that of composite with 10 wt% Gr. There was no clear difference in the friction reduction effect of NH and NT. The further addition of Gr to composites with NH or NT rather deteriorated the antiwear property of composites, although the friction coefficient was slightly reduced. The transferred materials existed on the friction surface of the mating ball, sliding against composites with three types of carbon filler. These transferred materials seemed to correlate with the low friction and wear properties of composites.
Photolysis of perfluoroazooctane with diamond powders led to chemical modification of the surface with the introduction of perfluorooctyl ester and ether functional groups, the presence of which was confirmed by means of FT-IR, XPS and 19F NMR measurements.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.