To correlate quantitatively the mechanical properties of precipitate free zones (PFZ) with the corresponding microstructural and compositional characteristics, TEM observation, EDX analysis and nanoindentation measurement have been performed in the vicinity of grain boundaries in Al -4.9 mass%Zn -1.8 mass%Mg (2 0.28 mass%Ag) alloys. The remarkable decreases in hardness and solute concentrations were observed towards grain boundaries even in the regions just outside PFZ. With increasing aging time, it is firstly revealed that the hardness inside PFZ monotonously decreases although the hardness inside grains increases in the earlier stage of aging. Three distinct regions of "PFZ", "Transition-area" and "Grain-region" were therefore proposed to explain the origins of such age-hardening behavior observed in this work. In the Ag-added alloy, on the other hand, the hardness could be maintained up to closer regions to grain boundaries at the same level as that inside grains. q
Dual phase 980 MPa grade (DP980) steel sheets were resistance spot welded using a pulsed current, and the effects of the pulsed current on the strength properties of the joints were investigated. The pulsed current improved the mechanical properties of the joints in cross tensile tests. In situ observations during tear tests revealed that the ductility of the nugget was improved and that the propagation of cracks into the nugget was inhibited when the pulsed current was used. Microstructural observations and electron probe microanalysis (EPMA) of the nugget showed that the segregation of phosphorus at the nugget was reduced in the joint welded using the pulsed current, suggesting that the pulsed current improved the ductility of the nugget by altering their microstructures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.