In this paper interdigitated electrodes for gas sensors were fabricated by inkjet printing technology. Silver electrodes were inkjet printed on Si/SiO 2 substrates instead of traditional photolithography method. The inkjet printing parameters to obtain desired dimensions, thickness of the electrodes and distance between the interdigitated electrodes were optimized in this study. The fabricated interdigitated silver electrodes were tested for application in ammonia gas sensors. Conductive polyaniline (PANI) layer was coated on the silver interdigitated electrodes by drop-coating. Ammonia detection of the PANI-coated chips was characterized with a gas measurement system in which humidity and ammonia concentrations were well-controlled. The electrical conductivity of the PANI films coated on the electrodes was measured when the PANI films were exposed to nitrogen and ammonia. The conductivity of the PANI films decreased significantly due to the deprotonation process of PANI upon ammonia expodure. The recovery time was about 15 min by heating up the polymer chip at 60 °C. The results showed that the silver electrodes fabricated by inkjet printing technique could be used as a sensor platform for ammonia detection.
pH sensitivity of emeraldine salt polyaniline (ES-PANI) and poly(vinyl butyral) (PVB) blend film was investigated. This blend film can be used as a pH sensing element in new-type pH sensors to replace traditional instruments based on fragile glass electrodes for pH measurement of water in aquaculture farming. Structural and optical characteristic of PANI were studied by Fourier transform infrared spectroscopy (FTIR) and ultraviolet visible spectroscopy (UV-vis). Electrical characterization of ES-PANI:PVB blend films versus pH was performed with chemiresistors fabricated by micro-lithography. A ES-PANI:PVB layer was drop-coated on comb-shaped platinum electrodes patterned on SiO 2 /Si substrates. Scanning electron microscope (SEM) and optical microscope were used to investigate morphology of the fabricated platinum electrodes and the coated polymer blend films. I-V measurements of the polymer-coated chemiresistors were performed at very low relative humidity after the polymer films were exposed to pH 1-8. The results showed that logarithm of electrical resistance of the ES-PANI:PVB films increased almost linearly as pH increased from 1 to 8. The initial results showed that the PANI blend-coated chemiresistors can be used as pH sensors for water quality monitoring.
Liposomal membrane disruption by means of miniaturized dielectric-barrier discharge in air: liposome characterization P Svarnas, L Asimakoulas, M Katsafadou et al.
AbstractMicro and nano liposome vesicles were prepared using a lipid film hydration method and a sonication method. Phospholipid, cholesterol and curcumin were used to form micro and nano liposomes containing curcumin. The size, structure and properties of the liposomes were characterized by using optical microscopy, transmission electron microscopy, and UV-vis and Raman spectroscopy. It was found that the size of the liposomes was dependent on their composition and the preparation method. The hydration method created micro multilamellars, whereas nano unilamellars were formed using the sonication method. By adding cholesterol, the vesicles of the liposome could be stabilized and stored at 4°C for up to 9 months. The liposome vesicles containing curcumin with good biocompatibility and biodegradability could be used for drug delivery applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.