Nanofibrous double-layer matrices were prepared by electrospinning technique with the bottom layer formed from PCL (poly-ε-caprolactone)/PLLA (poly-l-lactic acid) nanofibers and the upper layer from PCL/Gelatin nanofibers. Bottom layer was designed to give mechanical strength to the system, whereas upper layer containing gelatin was optimized to improve the cell adhesion. Gelatin microspheres were incorporated in the middle of two layers for controlled growth factor delivery. Successful fabrication of the blend nanofibers were shown by spectroscopy. Scanning electron microscopy results demonstrated that bead-free nanofibers with uniform morphology could be obtained by 10% w/v concentrations of PCL/PLLA and PCL/Gelatin solutions. Microspheres prepared by 15% gelatin concentration and cross-linked with 7.5% glutaraldehyde solution were chosen after in vitro release studies for the incorporation to the double-layer matrices. The optimized conditions were used to prepare fibroblast growth factor-2 (FGF-2) loaded microspheres. Preliminary cell culture studies showed that the FGF-2 could be actively loaded into the microspheres and enhanced the cell attachment and proliferation. The complete system had a slow degradation rate in saline (18% weight loss in 2 months) and it could meanwhile preserve its integrity. This sandwich system prevented microsphere leakage from the scaffold, and the hydrophilic and bioactive nature of the fibers at the upper layer promoted cell attachment to the surface. PLLA/PCL layer, on the other hand, improved the mechanical properties of the system and enabled better handling.
We report a synthesis route for the growth of Co:ZnO/ZnO core/shell quantum dots. This procedure consists of successive steps, comprising the addition of diluted precursor salt solutions, and heat treatment at 50 degrees C. By deriving a relation between the extinction coefficient at 250 nm and the nanocrystal diameter, we are able to monitor changes in quantum dot concentration during shell growth. We found that a mechanism based on the nucleation of new particles after salt addition and subsequent Ostwald ripening during the heat treatment is responsible for the shell growth. Based on ligand-field absorption spectroscopy, we demonstrate that the Co(2+) ions adsorbed at the surface of Co:ZnO quantum dots are incorporated inside the ZnO shells. Finally, EPR spectroscopy indicates that the surface-adsorbed Co(2+) ions can be incorporated as substitutional as well as interstitial Co(2+) ions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.