Efficient 3D cell systems for neuronal induction are needed for future use in tissue regeneration. In this study, we have characterized the ability of neural stem/progenitor cells (NS/PC) to survive, proliferate, and differentiate in a collagen type I-hyaluronan scaffold. Embryonic, postnatal, and adult NS/PC were seeded in the present 3D scaffold and cultured in medium containing epidermal growth factor and fibroblast growth factor-2, a condition that stimulates NS/PC proliferation. Progenitor cells from the embryonic brain had the highest proliferation rate, and adult cells the lowest, indicating a difference in mitogenic responsiveness. NS/PC from postnatal stages down-regulated nestin expression more rapidly than both embryonic and adult NS/PC, indicating a faster differentiation process. After 6 days of differentiation in the 3D scaffold, NS/PC from the postnatal brain had generated up to 70% neurons, compared with 14% in 2D. NS/PC from other ages gave rise to approximately the same proportion of neurons in 3D as in 2D (9-26% depending on the source for NS/PC). In the postnatal NS/PC cultures, the majority of betaIII-tubulin-positive cells expressed glutamate, gamma-aminobutyric acid, and synapsin I after 11 days of differentiation, indicating differentiation to mature neurons. Here we report that postnatal NS/PC survive, proliferate, and efficiently form synapsin I-positive neurons in a biocompatible hydrogel.
Here we present a novel injectable hydrogel which forms a template for de novo formation of bone tissue. Hydrogel formation takes place in situ in less than 1 min by the cross-linking of multifunctional hyaluronic acid and polyvinyl alcohol derivatives. Endogenous cells are recruited in vivo by incorporating bone morphogenetic protein-2 (BMP-2), a powerful promoter for osteogenic differentiation. The hydrogel was evaluated in vitro by performing a cell viability test and a release study and in vivo by a rat ectopic model. Examination by X-ray, microcomputed tomography, and histology revealed a significant bone formation at the target site for gels containing BMP-2, and a complete degradation was observed for gels without BMP-2 four weeks after injection. There were no signs of inflammation or foreign body response in either group and we believe that this system has the potential as an off-the-shelf injectable to be used where bone tissue is needed.
Linear poly(urethane urea) containing a biodegradable soft segment and a hard segment built solely from methyl-2,6-diisocyanatehexanoate (LDI) is presented, using a procedure where no chain extender is required. By having LDI in excess, together with a soft segment, and adding water in the vapor phase continuously creates amines in situ resulting in hard segments containing multiple LDI units linked via urea linkages. As soft segments, polymers of trimethylene carbonate (TMC) and copolymers of TMC, epsilon-caprolactone, and D,L-lactic acid (DLLA) were used. High inherent viscosity, 0.95-1.65 dL/g, was afforded even when DLLA-containing soft segments were used, which usually undergo aminolysis. With a hard segment content between 12% and 18%, all of the materials showed very high elongation at breakage, ranging from 1600% to 4700%, and an elastic modulus from 2.1 to 140 MPa. This one-pot synthesis is simple and has now been shown to be applicable to a large number of systems.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.