The short fatigue crack growth behaviour of a model cast aluminium piston alloy has been investigated. This has been achieved using a combination of fatigue crack replication methods at various intervals during fatigue testing and post-mortem analysis of the crack profiles. Crack-microstructure interactions have been clearly delineated using a combination of optical microscopy and scanning electron microscopy. Results show that intermetallic particles and eutectic Al-Si regions play a significant role in determining the crack path and growth rate of short fatigue cracks. It is observed that the growth of short cracks is often retarded or even arrested at intermetallic particles and Al-Si eutectic regions. Crack deflection at intermetallics and eutectic Si is also frequently observed. These results have been compared with the long crack growth behaviour of the alloy.
Among the several techniques for additive manufacturing (AM), fused deposition modelling (FDM) is widely used. Fused deposition modelling process uses a thermoplastic material, which is melted and then extruded layer by layer through a nozzle, in order to create a three‐dimensional object. As a result of the default setting of process parameters provided by the manufacturers, produced parts normally have a poor surface finish, low mechanical properties, low dimensional accuracy, and increased residual stresses compared to the parts produced using conventional manufacturing processes like molding (casting). Qualities of fused deposition modelled (FDMed) parts are generally affected by process parameters including the layer thickness, extrusion temperature, build orientation, printing speed, raster angle, infill density, raster width, nozzle diameter, and air gap. Increasing infill density, printing temperature, and decreasing print speed and layer thickness lead to increase mechanical strength and improve the surface finish of the printed parts. The optimal process parameters are preferred to achieve superior properties of the parts. This paper reviews the optimal fused deposition modelling process parameters on part qualities for making the stability of used deposition modelled parts for use. Various process parameters are identified in order to obtain desirable qualities in the manufactured parts. Areas for future research are proposed.
The short fatigue crack growth behaviour in a model cast aluminium piston alloy has been investigated. This has been achieved using a combination of fatigue crack replication methods at various intervals during fatigue testing and post‐mortem analysis of crack profiles. Crack–microstructure interactions have been clearly delineated using a combination of optical microscopy, scanning electron microscopy and electron backscatter diffraction. Results show that intermetallic particles play a significant role in determining the crack path and growth rate of short fatigue cracks. It is observed that the growth of short cracks is often retarded or even arrested at intermetallic particles and grain boundaries. Crack deflection at intermetallics and grain boundaries is also frequently observed. These results have been compared with the long crack growth behaviour of the alloy.
Recycled polypropylene filaments for fused filament fabrication were investigated with and without 14 wt% short fibre carbon reinforcements. The microstructure and mechanical properties of the filaments and 3D printed specimens were characterized using scanning electron microscopy and standard tensile testing. It was observed that recycled polypropylene filaments with 14 wt% short carbon fibre reinforcement contained pores that were dispersed throughout the microstructure of the filament. A two-stage filament extrusion process was observed to improve the spatial distribution of carbon fibre reinforcement but did not reduce the pores. Recycled polypropylene filaments without reinforcement extruded at high screw speeds above 20 rpm contained a centreline cavity but no spatially distributed pores. However, this cavity is eliminated when extrusion is carried out at screw speeds below 20 rpm. For 3D printed specimens, interlayer cavities were observed larger for specimens printed from 14 wt% carbon fibre reinforced recycled polypropylene than those printed from unreinforced filaments. The values of tensile strength for the filaments were 21.82 MPa and 24.22 MPa, which reduced to 19.72 MPa and 22.70 MPa, respectively, for 3D printed samples using the filaments. Likewise, the young's modulus of the filaments was 1208.6 MPa and 1412.7 MPa, which reduced to 961.5 MPa and 1352.3 MPa, respectively, for the 3D printed samples. The percentage elongation at failure for the recycled polypropylene filament was 9.83% but reduced to 3.84% for the samples printed with 14 wt% carbon fiber reinforced polypropylene filaments whose elongation to failure was 6.58%. The SEM observations on the fractured tensile test samples showed interlayer gaps between the printed and the adjacent raster layers. These gaps accounted for the reduction in the mechanical prop-How to cite this paper:
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.