Ionic liquid (IL)-hybrid organosilicas based on 1-n-butyl-3-(3-trimethoxysilylpropyl)-imidazolium cations associated with hydrophilic and hydrophobic anions decorated with well dispersed and similar sized (1.8-2.1 nm) Pd nanoparticles (PdNPs) are amongst the most active and selective catalysts for the partial hydrogenation of conjugated dienes to monoenes. The location of the sputter-imprinted Pd-NPs on different supports, as determined by RBS and HS-LEIS analysis, is modulated by the strength of the contact ion pair formed between the imidazolium cation and the anion, rather than the IL-hybrid organosilica pore size and surface area. In contrast, the pore diameter and surface area of the hybrid supports display a direct correlation with the anion hydrophobicity. XPS analysis showed that the Pd(0) surface component decreases with increasing ionic bond strength between the imidazolium cation and the anions (contact ion pair). The finding is corroborated by changes in the coordination number associated with the Pd-Pd scattering in EXAFS measurements. Hence, the interaction of the IL with the metal surface is found to occur via IL contact pairs (or aggregates). The observed selectivities of ≥99% to monoenes at full diene conversion indicate that the selectivity is intrinsic to the electron deficient Pd-metallic surfaces in this "restricted" ionic environment. This suggests that ILhybrid organosilica/Pd-NPs under multiphase conditions ("dynamic asymmetric mixture") operate akin to catalytically active membranes, i.e. far from the thermodynamic equilibrium. Detailed kinetic investigations show that the reaction rate is zero-order with respect to hydrogen and dependent on the fraction of catalyst surfaces covered by either the substrate and/or the product. The reaction proceeds via rapid inclusion and sorption of the diene to the IL/Pd metal surface saturated with H species. This is followed by reversible hydride migration to generate a π-allyl intermediate. The reductive elimination of this intermediate, the formal ratedetermining step (RDS), generates the alkene that is rapidly expelled from the IL phase to the organic phase.
Structural and morphological characterisation of bimetallic Pd-Pt/Al 2 O 3 model catalysts are performed using X-ray diffraction, X-ray absorption spectroscopy, transmission electron microscopy and CO chemisorption. Further, the catalysts were studied under oxidising and reducing conditions using both X-ray absorption spectroscopy and low-energy ion scattering spectroscopy. For the as-prepared catalysts, the existence of alloyed bimetallic Pd-Pt particles and of (tetragonal) PdO were found for the samples calcined at 800 C. PdO is present in form of crystals at the surface of the Pd-Pt particles or as isolated PdO crystals on the support oxide. Bimetallic Pd-Pt nanoparticles were only formed on the Pd-Pt catalysts after calcination at 800 C. The results show that the Pd-Pt nanoparticles undergo reversible changes in surface structure composition and chemical state in response to oxidising or reducing conditions. Under oxidising conditions Pd segregates to the shell and oxidises forming PdO, while under reducing conditions regions with metallic Pd and Pd-Pt alloys were observed at the surface.No bimetallic Pd-Pt nanoparticles were observed for the sample initially calcined at 500 C, but instead isolated monometallic particles, where small Pt particles are easily oxidised under O 2 treatment. In the monometallic catalysts, the Pd is found to be completely oxidised already after calcination and to consist of metallic Pd after reductive treatment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.