No abstract

Biosynthetic nerve grafts are desired as alternative to autologous nerve grafts in peripheral nerve reconstruction. Artificial nerve conduits still have their limitations and are not widely accepted in the clinical setting. Here we report an analysis of fine-tuned chitosan tubes used to reconstruct 10 mm nerve defects in the adult rat. The chitosan tubes displayed low, medium and high degrees of acetylation (DAI: ≈ 2%, DA: ≈ 5%, DAIII: ≈ 20%) and therefore different degradability and microenvironments for the regenerating nerve tissue. Short and long term investigations were performed demonstrating that the chitosan tubes allowed functional and morphological nerve regeneration similar to autologous nerve grafts. Irrespective of the DA growth factor regulation demonstrated to be the same as in controls. Analyses of stereological parameters as well as the immunological tissue response at the implantation site and in the regenerated nerves, revealed that DAI and DAIII chitosan tubes displayed some limitations in the support of axonal regeneration and a high speed of degradation accompanied with low mechanical stability, respectively. The chitosan tubes combine several pre-requisites for a clinical acceptance and DAII chitosan tubes have to be judged as the most supportive for peripheral nerve regeneration.

No abstract

No abstract

Running title: Chitosan guides for nerve repair 2 Tubulization with chitosan guides for the repair of long gap peripheral nerve injury in the rat. ABSTRACTBiosynthetic guides can be an alternative to nerve grafts for reconstructing severely injured peripheral nerves. The aim of this study was to evaluate the regenerative capability of chitosan tubes to bridge critical nerve gaps (15 mm long) in the rat sciatic nerve compared with silicone tubes and nerve autografts. Twenty-eight Wistar Hannover rats were randomly distributed into four groups (n=7 each) in which the nerve was repaied by: silicone tube (SIL), chitosan guides of low (~2%, DAI) and medium (~5%, DAII) degree of acetylation, and autograft (AG). Electrophysiological and algesimetry tests were performed serially along 4 month follow-up, and histomorphometric analysis was performed at the end of the study.Both groups with chitosan tubes showed similar degree of functional recovery, and similar number of myelinated nerve fibers at mid tube after 4 months of implantation. The results with chitosan tubes were significantly better compared to SIL tubes (P < 0.01), but lower than with AG (P < 0.01). In contrast to AG, in which all the rats had effective regeneration and target reinnervation, chitosan tubes from DAI and DAII achieved 43% and 57% success respectively, whereas regeneration failed in all the animals repaired with silicone tubes. This study suggests that chitosan guides are promising conduits to construct artificial nerve grafts.

Reconstruction of joint-crossing digital nerves requires the application of nerve guides with a much higher flexibility than used for peripheral nerve repair along larger bones. Nevertheless, collapse-resistance should be preserved to avoid secondary damage to the regrowing nerve tissue. In recent years, we presented chitosan nerve guides (CNGs) to be highly supportive for the regeneration of critical gap length peripheral nerve defects in the rat. Now, we evidently increased the bendability of regular CNGs (regCNGs) by developing a wavy wall structure, that is, corrugated CNGs (corrCNGs). In a comprehensive in vivo study, we compared both types of CNGs with clinical gold standard autologous nerve grafts (ANGs) and muscle-in-vein grafts (MVGs) that have recently been highlighted in the literature as a suitable alternative to ANGs. We reconstructed rat sciatic nerves over a critical gap length of 15 mm either immediately upon transection or after a delay period of 45 days. Electrodiagnostic measurements were applied to monitor functional motor recovery at 60, 90, 120, and 150 (only delayed repair) days postreconstruction. Upon explanation, tube properties were analyzed. Furthermore, distal nerve ends were evaluated using histomorphometry, while connective tissue specimens were subjected to immunohistological stainings. After 120 days (acute repair) or 150 days (delayed repair), respectively, compression-stability of regCNGs was slightly increased while it remained stable in corrCNGs. In both substudies, regCNGs and corrCNGs supported functional recovery of distal plantar muscles in a similar way and to a greater extent when compared with MVGs, while ANGs demonstrated the best support of regeneration. Anat Rec, 301:1697-1713, 2018. © 2018 Wiley Periodicals, Inc.

Various biomaterials have been proposed to build up scaffolds for promoting neural repair. Among them, chitosan, a derivative of chitin, has been raising more and more interestamongbasicandclinicalscientists.Anumberofstudieswithneuronalandglial cellcultures haveshownthat thisbiomaterial has biomimetic properties,which make it a good candidate for developing innovative devices for neural repair. Yet, in vivo experimental studies have shown that chitosan can be successfully used to create scaffolds that promote regeneration both in the central and in the peripheral nervous system. In this review, the relevant literature on the use of chitosan in the nervous tissue, either alone or in combination with other components, is overviewed. Altogether, the promising in vitro and in vivo experimental results make it possible to foresee that time for clinicaltrialswithchitosan-basednerveregenerationpromotingdevicesisapproaching quickly.

Grafting of encapsulated living cells has the potential to cure a wide variety of diseases. Large-scale application of the technique, however, is hampered by insufficient biocompatibility of the capsules. A major factor in the biocompatibility of capsules is inadequate covering of the inflammatory poly-L-lysine (PLL) on the capsules' surface. In the present study, we investigate whether tissue responses against alginate-PLL capsules can be reduced by crosslinking the surface of the capsules with heparin or polyacrylic acid. Our transplant study in rats shows a tissue response composed of fibroblasts and macrophages on alginate-PLL-alginate and alginate-PLL-heparin capsules that was completely absent on alginate-PLL-polyacrylic acid capsules. Atomic force microscopy analyses of the capsules demonstrates that the improved biocompatibility of alginate-PLL-capsules by polyacrylic acid coating should not only be explained by a more adequate binding of PLL but also by the induction of a smoother surface. This study shows for the first time that biologic responses against capsules can be successfully deleted by chemically crosslinking biocompatible molecules on the surface of alginate-PLL capsules.