Green electrospinning has attracted great interest since non-toxic solvents were shown to be applicable in the fabrication of fibrous materials while ensuring health safety and environmental protection. Less harmful reagents such as acetone (AC) and acetic acid (AA) have been employed in this field in recent years. However, research in this area is still rare, yielding only preliminary results. In this study, two different types of solvents (pure AC and an AA/AC mixture) were used to fabricate electrospun polycaprolactone (PCL) membranes. Sample morphology, wettability, tensile strength, and chemical composition were compared between two types of membranes. Cell-scaffold interaction was also examined by cell adhesion and proliferation assays. The results demonstrate that the two types of solvents had significant effects on membrane morphology, physical strength, and cell adherence behaviors, which should be considered for different application purposes.

In this study, the effect of coated hydrogel layer on characteristics of the whole gelatin/silver nanoparticles multi‐coated polycaprolactone membrane (PCLGelAg) was investigated through systematic and typical wound dressing characterizations to select the optimal number of layers for practical applications. Scanning electron microscopy, free swell absorptive capacity and tensile test in both wet and dry conditions were conducted to characterize all fabricated membranes of six coating times. In vitro cytotoxicity and agar diffusion evaluation were also carried out to assess the biocompatibility and antibacterial activity of the membranes. The findings illustrated that as the coated layers increase, the absorptive capacity, and degradation rate were higher, the membranes were stiffer in dry state while the tensile strength in wet state, elongation, and cell viability were significantly decreased. PCLGelAg3 was chosen to be the best fit for wound healing since it maintained quite sufficient maximum buffer uptake, elasticity, cell viability along with inducing abnormalities in bacterial morphology and preventing biofilm formation.