The nanotechnology field plays an important role in the improvement of dental implant surfaces. However, the different techniques used to coat these implants with nanostructured materials can differently affect cells, biomolecules and even ions at the nano scale level. The aim of this study is to evaluate and compare the structural, biomechanical and histological characterization of nano titania films produced by either modified laser or dip coating techniques on commercially pure titanium implant fixtures. Grade II commercially pure titanium rectangular samples measuring 35 × 12 × 0.25 mm length, width and thickness, respectively were coated with titania films using a modified laser deposition technique as the experimental group, while the control group was dip-coated with titania film. The crystallinity, surface roughness, histological feature, microstructures and removal torque values were investigated and compared between the groups. Compared with dip coating technique, the modified laser technique provided a higher quality thin coating film, with improved surface roughness values. For in vivo examinations, forty coated screw-designed dental implants were inserted into the tibia of 20 white New Zealand rabbits' bone. Biomechanical and histological evaluations were performed after 2 and 4 weeks of implantation. The histological findings showed a variation in the bone response around coated implants done with different coating techniques and different healing intervals. Modified laser-coated samples revealed a significant improvement in structure, surface roughness values, bone integration and bond strength at the bone-implant interface than dip-coated samples. Thus, this technique can be an alternative for coating titanium dental implants.
The clinical success of dental implants can be improved by achieving optimum implant properties, such as their biomechanical and surface characteristics. Nano-structured coatings can play an important role in improving the implant surface. The purpose of the present study was to determine the most appropriate conditions for electrophoretic deposition (EPD) of nano-zirconia coatings on Ti-6Al-7Nb substrates and to evaluate the structural and biomechanical characteristics of these deposited coatings on the dental implants. EPD was used with different applied voltages and time periods to obtain a uniform layer of nano-zirconia on Ti-6Al-7Nb samples. The coated samples were weighed and the thickness of the product layer was measured. Surface analysis was performed by using optical microscopical examination, scanning electron microscope and X-ray diffraction phase analysis. For in vivo examination, 48 screw-designed implants (24 uncoated and 24 nano-zirconia coated) were implanted in both tibiae of 12 white New Zealand rabbits and evaluated biomechanically after 4- and 12-week healing intervals. Results revealed that the use of different conditions for EPD affected the final coating film properties. Increasing the applied voltage and coating time period increased the deposited nano-zirconia film thickness and weight. By selecting the appropriate coating conditions, and analyzing scanning electron microscopical examination and XRD patterns, this technique could produce a thin and continuous nano-zirconia layer with a uniform thickness of the Ti-6Al-7Nb samples. Mechanically, the nano-zirconia-coated implants showed a highly statistically significant difference in removal torque values, while histologically these coated implants enhanced and promoted osseointegration after 4 and 12 weeks of healing, compared with the uncoated ones. In conclusion, EPD is an effective technique for providing a high quality nano-zirconia coating film on dental implant surfaces. Moreover, the osseointegration of these coated dental implants is improved compared with that of uncoated ones.
Background. Implant insertion in regions with poor bone quantity, such as the posterior maxilla, is potentially associated with an increased rate of implant failure. Calcium sulfate can be used as the coating material for commercially pure titanium (CpTi) and as the bone graft material around implants when bound to eggshell powder to enhance the bone quality and quantity of bone defect regions. This study performed a torque removal test to evaluate the effectiveness of eggshell powder as a bone substitute for filling bone defects around CpTi-coated implants coated with nanocrystalline calcium sulfate. Materials and Methods. Eighty screw implant designs were used in the tibiae of 20 white New Zealand rabbits. A total of uncoated 20 screws constituted the control group, and the remaining 60 screws coated with nano calcium sulfate nanoparticles were used as the experimental groups as follows: 20 screws coated with nano calcium sulfate were used alone in the tibiae without gaps around them, 20 screws coated with nano calcium sulfate were used with the gaps made around them and filled with eggshell powder as the bone graft material, and 20 screws coated with nano calcium sulfate were used with the gaps made around them left unfilled. Results. After 2 to 6 weeks of healing, a significant improvement in bone regeneration and an increase in torque removal values were observed when the bone defect around the CpTi implant coated with nano calcium sulfate was filled with eggshell powder as the bone substitute. Conclusions. Nano calcium sulfate particles applied through the dip-coating method can successfully work as the coating material of CpTi implants. These particles work in synergy with eggshell powder to act as the bone graft around the implants.
Aim: To evaluate the wettability and microhardness of Zirconium (ZrO2) dental material when coated with different concentrations of Faujasite. Materials and methods: 30 circular disks produced from ZrO2, then each group is classified into 10 control groups, 10 coated groups with 3% Faujasite, and 10 coated groups with 7% faujasite by electro-spun tool to study variable properties in hardness and water contact angle of implant materials. Results: This study stated the high hardness in 7% of faujasite concentration for ZrO2, in addition, the contact angle decreased gradually until reach 0 ᵒ in 7% concentration of faujasite with ZrO2 Conclusion: Water contact angle (WCA) declined till disappeared in (7% wt.) of faujasite coated with the ZrO2 group, also in the same group the microhardness became high compared with other groups due to alteration in surface morphology of substrate, and properties of coated material.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.