Polypropylene (PP) has the most extensive plastics of plastics because of the advantages of simplicity, easy processing, high mechanical properties, high corrosion resistance and abrasion resistance and electrical insulation. The application of PP has limitations in many fields because it is lack of formation shrinkage, low modulus, poor thermal stability, strong gap and low temperature and cracking. The addition of mineral fillers can not only improve their performance, not just the PP/mineral filler composite materials required, but also reduce the cost of the material. Therefore, in this paper, lamellar mica was selected as mineral filler to modify the surface of PP. The effects of titanate coupling agent and silane coupling agent modified mica, and their addition on the properties of PP were systematically studied. KH-570 modification increases the tensile strength, bending strength and modulus of the composites, while JN-114 and KH-570 can effectively improve the toughness and processability of PP composites. The interaction between modifier and mica was analyzed comprehensively by infrared spectroscopy (FTIR), and the effect mechanism of mica on the properties of PP was discussed by scanning electron microscope. The results show that different modified mica as mineral filler and PP can produce synergistic effect.
In this paper, the method of filling natural rubber with zeolite as filler was mainly studied in the following two aspects: firstly, experiments selected organic amine surface modifier to modify natural zeolite and used infrared spectroscopy to analyze the interaction between the modifier and zeolite, and secondly, studying the application of modified zeolite in natural rubber and using scanning electron microscopy to analyze the mechanism of action between zeolite and natural rubber. The test results show that octadecylamine in the modifier had the relatively best effect. Under the best conditions, the activation index of the modified product could reach 95% and above, and the contact angle could reach about 100°. When the filling amount was 30 phr, the octadecylamine modification had the most obvious effect on the performance of zeolite/natural rubber and the composite rubber had better mechanical properties. The corresponding tensile strength, tear strength, elongation at break and Shore hardness were 22.59 MPa, 28.52 MPa, 782.1% and 41, respectively, which were 45.74%, 19.28%, 7.95% and 7.89% higher than those of unmodified zeolite/natural rubber. As the first study of organic amine modified zeolite as a filler for filling natural rubber, this work provides a new way to improve the added value of natural zeolite.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.