Objective: This study evaluated the effect of food-simulating media associated with brushing and coffee staining on color stability of different composite resins. Materials and methods: Eighty specimens were prepared for each composite: Grandio SO (Voco), Amaris (Voco), Filtek Z350XT (3M/ESPE), Filtek P90 (3M/ESPE). They were divided into four groups according to food-simulating media for 7 days: artificial saliva (control), heptane, citric acid and ethanol. The composite surface was submitted to 10,950 brushing cycles (200 g load) in an automatic toothbrushing machine. The specimens were darkened with coffee solution at 37 °C for 24 h. After each treatment, color measurements were assessed by spectrophotometry, using CIE L*a*b* system. The overall color change (ΔE) was determined for each specimen at baseline (C1) and after the treatments (food-simulating media immersion/C2, brushing/C3 and dye solution/C4). Data were analyzed by two-way repeated measures ANOVA and Tukey’s tests (p < .05). Results: The results of RM-ANOVA showed significant differences for composites (p = .001), time (p = .001) and chemical degradation (p = .002). The mean of ΔE for composites were: Z350XT (5.39)a, Amaris (3.89)b, Grandio (3.75)bc, P90 (3.36)c. According to food-simulating media: heptane (4.41)a, citric acid (4.24)a, ethanol (4.02)ab, artificial saliva (3.76)b. For the treatments: dye solution (4.53)a, brushing (4.26)a, after food-simulating media (3.52)b. Conclusions: The composite resin Filtek Z350XT showed significantly higher staining than all other composite resin tested. The immersion in heptane and citric acid produced the highest color alteration than other food-simulating media. The exposure of samples to brushing protocols and darkening in coffee solution resulted in significant color alteration of the composite resins.
The necessity in standardization of methodologies to enable a comparison among researches.
Background/purpose The primeval evaluation of the properties of composite resins with different compositions that impact clinical behavior is very important in guiding use in clinical settings. The aim of this study was to evaluate color stability (ΔE) and Knoop microhardness (KHN) of composite resins containing different compositions. Materials and methods Forty-five disks were made composite resins: Filtek Z350 XT/3MESPE and Beautifill II/SHOFU and divided into 3 subgroups: Control - immersed in artificial saliva; OB – brushing with Oral B 3D White; CT - brushing with Colgate Total 12. The OB and CT groups had the disks brushed daily with 120 cycles after immersion in coffee solution (10 min) for a period of 30 days. ΔE and KHN was obtained at baseline and after the treatments. Data were analyzed ANOVA and Tukey tests ( p < 0.05). Results ANOVA revealed significant differences for ΔE and KHN. ΔE: the highest mean was observed in Beautifil II composite resin group, which differed significantly from Z350 group. For the Beautifil II, the treatments were significantly different from each other. For the Z350, the control group showed significant differences in relation to OB e CT groups. KHN: the highest mean was observed in Z350 group, which differed significantly from Beautifil II group. For Z350, the control group showed significant differences in relation to OB e CT groups. For Beautifil II, the treatments did not differ significantly among themselves. Conclusion The composite resin containing fluoride in the composition showed higher color alteration (ΔE) and lower Knoop microhardness (KHN), thus demonstrating that composition is an important factor in the clinical performance of esthetic restorative materials.
SUMMARY Objectives: This study aimed to evaluate the bonding performance of a universal adhesive used according to self-etching or etch-and-rinse protocols in noncarious cervical lesions (NCCLs) and to compare the two protocols with their respective gold standard techniques. Methods and Materials: This randomized, double-blind clinical study enrolled 34 participants who met the inclusion criteria, 29 of whom returned after two years. They received 152 restorations bonded with one of the three adhesives (Scotchbond Universal Adhesive, Adper Single Bond 2, or Clearfil SE Bond) and one of the two bonding techniques tested. The NCCLs were restored with nanocomposite resin (Filtek Supreme). Final contours were done with a fine diamond rotary instrument and polished with rubber points. The restorations were evaluated using the FDI World Dental Federation criteria at baseline (seven days after the restoration procedure), 6, 12, and 24 months. Descriptive statistics, Kruskal-Wallis, Friedman analysis of variance, and least significant difference tests were performed. Results: No statistically significant differences were found in esthetics or the functional and biological evaluated criteria among the adhesive systems and techniques. Conclusions: The Scotchbond Universal system behaved similarly to the conventional etch-and-rinse or self-etching systems in all the adhesion strategies in the evaluated periods.
The aim of this study was to evaluate the effects of simulated pulpal pressure (SPP) on the variation of intrapulpal temperature (ΔT) and microtensile bond strength (μTBS) to dentin submitted to an adhesive technique using laser irradiation. One hundred sound human molars were randomly divided into two groups (n = 50), according to the presence or absence of SPP (15 cm H2O). Each group was divided into five subgroups (n = 10) according to Nd:YAG laser energy (60, 80, 100, 120, 140 mJ/pulse). The samples were sequentially treated with the following: 37 % phosphoric acid, adhesive (Scotchbond Universal), irradiation with Nd:YAG laser (60 s), and light curing (10 s). ΔT was evaluated during laser irradiation using a type K thermocouple. Next, a composite resin block was build up onto the irradiated area. After 48 h, samples were submitted to microtensile test (10 kgf load cell, 0.5 mm/min). Data were analyzed by two-way ANOVA and Tukey tests (p = 0.05). ANOVA revealed significant differences for ΔT and TBS in the presence of SPP. For ΔT, the highest mean (14.3 ± 3.23 °C)(A) was observed in 140 mJ and without SPP. For μTBS, the highest mean (33.4 ± 4.15 MPa)(A) was observed in 140 mJ and without SPP. SPP significantly reduced both ΔT and μTBS during adhesive procedures, lower laser energy parameters resulted in smaller ΔT, and the laser parameters did not influence the μTBS values.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.