This study reports light energy harvesting characteristics of bismuth ferrite (BiFeO3) and BiFO3 doped with rare-earth metals such as neodymium (Nd), praseodymium (Pr), and gadolinium (Gd) dye solutions that were prepared by using the co-precipitation method. The structural, morphological, and optical properties of synthesized materials were studied, confirming that 5–50 nm sized synthesized particles have a well-developed and non-uniform grain size due to their amorphous nature. Moreover, the peaks of photoelectron emission for bare and doped BiFeO3 were observed in the visible region at around 490 nm, while the emission intensity of bare BiFeO3 was noticed to be lower than that of doped materials. Photoanodes were prepared with the paste of the synthesized sample and then assembled to make a solar cell. The natural and synthetic dye solutions of Mentha, Actinidia deliciosa, and green malachite, respectively, were prepared in which the photoanodes were immersed to analyze the photoconversion efficiency of the assembled dye-synthesized solar cells. The power conversion efficiency of fabricated DSSCs, which was confirmed from the I–V curve, is in the range from 0.84 to 2.15%. This study confirms that mint (Mentha) dye and Nd-doped BiFeO3 materials were found to be the most efficient sensitizer and photoanode materials among all the sensitizers and photoanodes tested.
In this study, Fe2O3 powder was synthesized using the co-precipitation method from scrap iron, which was then treated with varying concentrations of copper. Afterwards, the modified Fe2O3 was reinforced in the PVC matrix by using the solution-casting method to synthesize PVC composite films, which were subjected to a UV-visible spectrophotometer, a Fourier transform infrared spectrophotometer, an X-ray diffractometer, and a thermal gravimetric analyzer to evaluate the optical, chemical, structural, and thermal properties. FTIR analysis reveals the formation of the composite through vibrational bands pertaining to both components present, whereas no significant changes in the XRD patterns of PVC were observed after the doping of modified iron oxide, which reveals the compatibility of fillers with the PVC matrix. The optical properties of the copper-doped iron oxide-PVC composites, including absorbance, refractive index, urbach energy, and optical as well as electrical conductivity are measured, and show an increase in optical activity when compared to the pure PVC compound. Moreover, the increased thermal stability of the synthesized composite was also observed and compared with conventional compounds, which, in accordance with all the other mentioned properties, makes the copper-dopped iron oxide-PVC composite an effective material for electronic, photonic, and optical device applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.