Excessive demineralization in osteoporotic bones impairs its self-regeneration potential following a defect/fracture and is of great concern among the aged population. In this context, implants with inherent osteogenic ability loaded with therapeutic ions like Strontium (Sr) may bring forth promising outcomes. Micro-granular Strontium incorporated Hydroxyapatite scaffolds have been synthesized and in vivo osteogenic efficacy was evaluated in a long-term osteoporosis-induced aged (LOA) rat model. Micro-granules with improved surface area are anticipated to resorb faster and together with the inherent bioactive properties of Hydroxyapatite with the leaching of Strontium ions from the scaffold, osteoporotic bone healing may be promoted. Long-term osteoporosis-induced aged rat model was chosen to extrapolate the results to clinical osteoporotic condition in the aged. Micro-granular 10% Strontium incorporated Hydroxyapatite synthesized by wet precipitation method exhibited increased in vitro dissolution rate and inductively coupled plasma studies confirmed Strontium ion release of 0.01 mM, proving its therapeutic potential for osteoporotic applications. Wistar rats were induced to long-term osteoporosis-induced aged model by ovariectomy along with a prolonged induction period of 10 months. Thereafter, osteogenic efficacy of Strontium incorporated Hydroxyapatite micro-granules was evaluated in femoral bone defects in the long-term osteoporosis-induced aged model. Post eight weeks of implantation in vivo regeneration efficacy ratio was highest in the Strontium incorporated Hydroxyapatite implanted group (0.92 ± 0.04) compared to sham and Hydroxyapatite implanted group. Micro CT evaluation further substantiated the improved osteointegration of Strontium incorporated Hydroxyapatite implants from the density histograms. Thus, the therapeutical potential of micro-granular Strontium incorporated Hydroxyapatite scaffolds becomes relevant, especially as bone void fillers in osteoporotic cases of tumor resection or trauma.

No abstract

No abstract

No abstract

type microporous silico alumino phosphate SAPO-35 are synthesized by using hydrothermal method. TiO 2 /SAPO-35 nanocomposites were prepared by solgel method with different weight ratios. The synthesized materials were characterized by various analytical techniques such as PXRD, SEM/EDAX, TG/DTA, BET-Surface area, FT-IR, UV-Vis, XPS, MAS-NMR and photocatalytic study. From PXRD results it clearly evidenced that, the TiO 2 anatase peaks and SAPO-35 combined peaks are in the composite. The spherical shaped TiO 2 nanoparticles were found to be dispersed over the rhombohedral SAPO-35 particles, which was analysed by SEM. BET-surface area analysis revealed that, the calcined SAPO-35 has the surface area of 448 m 2 /g, was decreased to 222 m 2 /g for composite which is due to the presence of TiO 2 particles having surface area of 85 m 2 /g on the surface of SAPO-35. The oxidation state and co-ordination of various elements present in nanocomposite was composed by X-ray photoelectron spectroscopy. MAS-NMR analysis has shown that SAPO-35 has tetrahedral Al, P and Si oxides. Eventhough Al is unique Si and P are in two different environment namely one in S6R and another in D6R with double intensity. The photocatalytic performance of methylene blue degradation under sunlight radiation by the synthesized TiO 2 /SAPO-35 was analyzed. The TiO 2 /SAPO-35 composites degrade the methylene blue under sunlight irradiation in 25 minutes against 90 minuts for pure TiO 2 anatase. A plausible mechanism on photocatalytic activity is also proposed.

No abstract

In the present study, we synthesized several high-surface area V2O5/TiO2–SiO2 catalysts (vanado titanium silicate, VTS). The synthesized materials are characterized by PXRD, FE-SEM/EDAX, TEM, BET-surface area, FT-IR, UV-Vis, XPS, fluorescence and photocatalytic studies.

No abstract