White spot lesions (WSLs), a side effect of orthodontic treatment, can result in reversible and unaesthetic results. Graphene oxide (GO) with a bioactive glass (BAG) mixture (BAG@GO) was added to Low-Viscosity Transbond XT (LV) in a ratio of 1, 3, and 5%. The composite’s characterization and its physical and biological properties were verified with scanning electron microscopy (SEM) and X-ray diffraction (XRD); its microhardness, shear bond strength (SBS), cell viability, and adhesive remnant index (ARI) were also assessed. Efficiency in reducing WSL was evaluated using antibacterial activity of S. mutans. Anti-demineralization was analyzed using a cycle of the acid-base solution. Adhesives with 3 wt.% or 5 wt.% of BAG@GO showed significant increase in microhardness compared with LV. The sample and LV groups showed no significant differences in SBS or ARI. The cell viability test confirmed that none of the sample groups showed higher toxicity compared to the LV group. Antibacterial activity was higher in the 48-h group than in the 24 h group; the 48 h test showed that BAG@GO had a high antibacterial effect, which was more pronounced in 5 wt.% of BAG@GO. Anti-demineralization effect was higher in the BAG@GO-group than in the LV-group; the higher the BAG@GO concentration, the higher the anti-demineralization effect.
Despite the convenience of bulk filling, careful selection of BFC is advised because some BFCs have worse microhardness and polymerization shrinkage than RBCs due to their lower filler contents.
Lasers have many favorable features as a light source owing to their monochromaticity and coherence. This study examined the mechanical properties of composite resins that were light-cured using a diode-pumped solid state (DPSS) laser. Eight composite resins were light-cured using four different light sources (one quartz-tungsten-halogen (QTH), two light-emitting diodes (LEDs), and one DPSS laser with a wavelength of 473 nm). The light intensity of the DPSS laser and remaining light-curing units were approximately 500 and 900 mW/cm(2), respectively. The microhardness, flexural properties, and compressive properties were evaluated using the Vickers hardness test, three-point bending test, and compression test, respectively. In most cases, the microhardness, flexural properties, and compressive properties of the specimens light-cured using the DPSS laser were similar to those obtained using the other light-curing units. Within the limits of the study, the microhardness, flexural modulus, and compressive strength were linearly correlated with the filler content (in weight percent). The flexural modulus and compressive modulus were also linearly correlated with the microhardness. Even with a much lower light intensity, the DPSS laser with a wavelength of 473 nm can polymerize composite resins and give comparable mechanical properties to those obtained using the other light-curing units.
The selection of a light-curing unit for the curing composite resins is important to achieve best outcomes. The purpose of the present study was to test lasers of 457 and 473 nm alone or in combination under different light conditions with respect to the cure of composite resins. Four different composite resins were light cured using five different laser combinations (530 mW/cm(2) 457 nm only, 530 mW/cm(2) 473 nm only, 177 mW/cm(2) 457 + 177 mW/cm(2) 473 nm, 265 mW/cm(2) 457 + 265 mW/cm(2) 473 nm, and 354 mW/cm(2) 457 + 354 mW/cm(2) 473 nm). Microhardness and polymerization shrinkage were evaluated. A light-emitting diode (LED) unit was used for comparison purposes. On top surfaces, after aging for 24 h, microhardness achieved using the LED unit and the lasers with different conditions ranged 42.4-65.5 and 38.9-67.7 Hv, respectively, and on bottom surfaces, corresponding ranges were 25.2-56.1 and 18.5-55.7 Hv, respectively. Of the conditions used, 354 mW/cm(2) 457 nm + 354 mW/cm(2) 473 nm produced the highest bottom microhardness (33.8-55.6 Hv). On top and bottom surfaces, microhardness by the lowest total light intensity, 354 (177 × 2) mW/cm(2), ranged 39.0-60.5 and 18.5-52.8 Hv, respectively. Generally, 530 mW/cm(2) at 457 nm produced the lowest polymerization shrinkage. However, shrinkage values obtained using all five laser conditions were similar. The study shows the lasers of 457 and 473 nm are useful for curing composite resins alone or in combination at much lower light intensities than the LED unit.
Objective: The purpose of the present study was to test the usefulness of 457 nm diode-pumped solid state (DPSS) laser as a light source to cure composite resins. Materials and methods: Five different composite resins were light cured using three different light-curing units (LCUs): a DPSS 457 nm laser (LAS), a light-emitting diode (LED), and quartz-tungsten-halogen (QTH) units. The light intensity of LAS was 560 mW/cm 2 , whereas LED and QTH LCUs was *900 mW/cm 2 . The degree of polymerization was tested by evaluating microhardness, cross-link density, and polymerization shrinkage. Results: Before water immersion, the microhardness of laser-treated specimens ranged from 40.8 to 84.7 HV and from 31.7 to 79.0 HV on the top and bottom surfaces, respectively, and these values were 3.3-23.2% and 2.9-31.1% lower than the highest microhardness obtained using LED or QTH LCUs. Also, laser-treated specimens had lower top and bottom microhardnesses than the other LCUs treated specimens by 2.4-19.4% and 1.4-27.8%, respectively. After ethanol immersion for 24 h, the microhardness of laser-treated specimens ranged from 20.3 to 63.2 HV on top and bottom surfaces, but from 24.9 to 71.5 HV when specimens were cured using the other LCUs. Polymerization shrinkage was 9.8-14.7 lm for laser-treated specimens, and these were significantly similar or lower (10.2-16.0 lm) than those obtained using the other LCUs. Conclusions: The results may suggest that the 457 nm DPSS laser can be used as a light source for light-curing dental resin composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.