The aim of this in vitro study was to evaluate five commonly used soft lining materials, Viscogel (VG), Ufi Gel P (UGP), Softliner (S), Coe-Soft (CS), and Molloplast-B (MB) in terms of cytotoxicity by MTT assay, using L929 mouse fibroblasts. Sixteen disk-shaped specimens from each material were prepared (according to the manufacturer's instructions) in stainless steel mold (10 mm diameter and 1.5 mm thick). The specimens were incubated for 24, 48, 72, and 96 h in Dulbecco's Modified Eagle Medium Ham's F12 (DMEM/F12) and following each incubation interval, cytotoxicity of the extracts to cultured mouse fibroblasts (L929) were measured by MTT assay. Data were statistically analyzed by two-way analysis of variance (ANOVA), and Duncan's test, at a significance level of p < 0.05. Group CS revealed significantly high cytotoxic effect at all incubation periods (p < 0.05). Although no cytotoxic effect for Group S was found at 24, 48, 72 h periods, it has been raised at 96-h incubation period (p > 0.05). Group VG, UGP, S (except at 96 h period), and Group MB demonstrated high cell survival rates at incubation periods.

The composite resins used in this study were cytotoxic after 48 h pre-incubation, but this toxicity disappeared after pre-incubation in a biological medium for 7 days. Curing did not have a significant effect on the cytotoxicity of the composite materials tested.

No abstract

The aim of this study was to determine the transportations of rivastigmine containing from various liposome formulations through Madin Darby Canine Kidney (MDCK) cells monolayer and to compare the in vitro test results with in vivo. There is no other liposome formulation of rivastigmine and the transportations of rivastigmine through MDCK cell monolayers or related study available in the literature. Cytotoxicity (MTT) test was used to determine cell viabilities. The effect of sodium-taurocholate or dimethyl-beta-cyclodextrine as penetration enhancer was also investigated. Characterization and stability studies for liposome formulations were performed. Permeation experiments of rivastigmine were performed through MDCK cells and dialysis membrane. The kinetic of release from liposomes was also investigated. The highest apparent permeability coefficient (log. values) was obtained with sodium-taurocholate liposomes for -1.15 ± 0.16 for MDCK cell. Rivastigmine liposomes and solutions were also administered to mice orally and intraperitonally. Acetylcholinesterase (AChE) activity was determined by Ellman method. AChE% inhibition values were calculated for both blood and brain after administration of rivastigmine solution and liposomes. The highest AChE inhibition was observed for rivastigmine-sodium-taurocholate liposomes. Histological observations of the mice' brains were performed under transmission electron microscope (TEM). The histological results were also indicated and supported all these findings.

ObjectiveApplications of resin luting agents and high-power light-emitting diodes (LED) light-curing units (LCUs) have increased considerably over the last few years. However, it is not clear whether the effect of reduced exposure time on cytotoxicity of such products have adequate biocompatibility to meet clinical success. This study aimed at assessing the effect of reduced curing time of five resin luting cements (RLCs) polymerized by high-power LED curing unit on the viability of a cell of L-929 fibroblast cells.Material and MethodsDisc-shaped samples were prepared in polytetrafluoroethylene moulds with cylindrical cavities. The samples were irradiated from the top through the ceramic discs and acetate strips using LED LCU for 20 s (50% of the manufacturer's recommended exposure time) and 40 s (100% exposure time). After curing, the samples were transferred into a culture medium for 24 h. The eluates were obtained and pipetted onto L-929 fibroblast cultures (3x104 per well) and incubated for evaluating after 24 h. Measurements were performed by dimethylthiazol diphenyltetrazolium assay. Statistical significance was determined by two-way ANOVA and two independent samples were compared by t-test.ResultsResults showed that eluates of most of the materials polymerized for 20 s (except Rely X Unicem and Illusion) reduced to a higher extent cell viability compared to samples of the same materials polymerized for 40 s. Illusion exhibited the least cytotoxicity for 20 s exposure time compared to the control (culture without samples) followed by Rely X Unicem and Rely X ARC (90.81%, 88.90%, and 83.11%, respectively). For Rely X ARC, Duolink and Lute-It 40 s exposure time was better (t=-1.262 p=0,276; t=-9.399 p=0.001; and t=-20.418 p<0.001, respectively).ConclusionThe results of this study suggest that reduction of curing time significantly enhances the cytotoxicity of the studied resin cement materials, therefore compromising their clinical performance.

No abstract

The purpose of this in vitro study was to evaluate the cytotoxicity of three maxillofacial silicone elastomers at 24, 48, and 72 h on L-929 cells and to determine the effect of accelerated aging on the cytotoxicity of these silicone elastomers. Disc-shaped test samples of maxillofacial silicone elastomers (Cosmesil, Episil, Multisil) were fabricated according to manufacturers' instructions under aseptic conditions. Samples were then divided into three groups: (1) not aged; (2) aged for 150 h with an accelerated weathering tester; and (3) aged for 300 h. Then the samples were placed in Dulbecco's Modified Eagle Medium/Ham's F12 (DMEM/F12) for 24, 48, and 72 h. After the incubation periods, cytotoxicity of the extracts to cultured fibroblasts (L-929) was measured by MTT assay. The degree of cytotoxicity of each sample was determined according to the reference value represented by the cells with a control (culture without sample). Statistical significance was determined by repeated measurement ANOVA (p < 0.01) followed by Duncan's test (p < 0.05). All test materials in each group demonstrated high survival rates in MTT assay (Episil; 93.84%, Multisil; 88.30%, Cosmesil; 87.50%, respectively); however, in all groups, Episil material demonstrated significantly higher cell survival rate after each of the experimental incubation periods (p < 0.05). Accelerated aging for 150 and 300 h had no significant effect on the biocompatibility of maxillofacial silicone elastomers tested (p > 0.05).

Six new platinum(II) complexes with 1-H or methyl-2-chloromethyl or acetoxymethyl or 2'-hydroxyethylbenzimidazole carrier ligands were synthesized and evaluated for their reactivity against model nucleophile I(-), cellular uptake, and in vitro antiproliferative activities against the human MCF-7 breast and HeLa cervix cancer cell lines. The effect of the compounds on pBR322 plasmid DNA was studied by gel electrophoretic mobility measurements. Flow cytometric analysis was also carried out to study the effect of representative compounds 1 and 2, bearing 2-chloromethyl or -acetoxymethylbenzimidazole carrier ligands, on the cell cycle distribution of MCF-7 and HeLa cells, respectively. In general, it was found that Pt(II) complexes were less cytotoxic than cisplatin and were comparable to carboplatin. The results of the plasmid DNA interaction and the restriction studies suggest that changing the chemical structure of the benzimidazole ligands may modulate DNA binding mode and the sequence selectivity. Compounds 1 and 2 had no significant effect on the cell cycle profile of the cells used. However, compound 2 induced a significant increase in the SubG1 cell population at a concentration of 20 microM.