Poly(lactic acid) (PLA) and poly(ethylene glycol) (PEG) were melt-blended and extruded into films in the PLA/PEG ratios of 100/0, 90/10, 70/30, 50/50, and 30/ 70. It was concluded from the differential scanning calorimetry and dynamic mechanical analysis results that PLA/PEG blends range from miscible to partially miscible, depending on the concentration. Below 50% PEG content the PEG plasticized the PLA, yielding higher elongations and lower modulus values. Above 50% PEG content the blend morphology was driven by the increasing crystallinity of PEG, resulting in an increase in modulus and a corresponding decrease in elongation at break. The tensile strength was found to decrease in a linear fashion with increasing PEG content. Results obtained from enzymatic degradation show that the weight loss for all of the blends was significantly greater than that for the pure PLA. When the PEG content was 30% or lower, weight loss was found to be primarily due to enzymatic degradation of the PLA. Above 30% PEG content, the weight loss was found to be mainly due to the dissolution of PEG. During hydrolytic degradation, for PLA/PEG blends up to 30% PEG, weight loss occurs as a combination of degradation of PLA and dissolution of PEG.

Citrate esters were used as plasticizers with poly(lactic acid) (PLA). Films were extruded using a single-screw extruder with plasticizer contents of 10, 20, and 30% by weight. All of the citrate esters investigated were found to be effective in reducing the glass transition temperature and improving the elongation at break. It was observed that the plasticizing efficiency was higher for the intermediate-molecularweight plasticizers. Hydrolytic and enzymatic degradation tests were conducted on these films. It was found that the lower-molecular-weight citrates increased the enzymatic degradation rate of PLA and the higher-molecular-weight citrates decreased the degradation rate as compared with that of unplasticized PLA.

No abstract

No abstract

No abstract

No abstract

No abstract