Photo-active layers from non-stabilized P3HT:ICBA nanoparticles enable the fabrication of inverted organic solar cells from eco-friendly, alcoholic dispersions. Exhibiting power conversion efficiencies (PCEs) ≈4%, the devices are competitive to state-of-the-art P3HT:ICBA solar cells from chlorinated solvents. Upon thermal annealing, the short circuit current density and consequently the PCE of the inverted solar cells improve radically due to a more intimate contact of the nanoparticles and hence an enhanced charge carrier extraction.

No abstract

A fullerene was covalently attached to a (dA)20 template that serves as structural scaffold to self-assemble an ordered and mixed array of ethynyl-pyrene- and ethynyl-Nile-red-nucleoside conjugates. Fluorescence spectroscopy revealed evidence for energy transfer between the two different chromophores. Moreover, fluorescence quenching is significantly enhanced by the attached fullerene in mixed assemblies of different chromophore ratios. This indicates exciton dissociation by electron transfer from the photo-generated exciton on the chromophore stack to the fullerene. The fullerene-DNA-conjugate was integrated as a photo-active layer in solar cells that showed charge-carrier generation in the spectral regime of all three components of the conjugate. This work clearly demonstrates that DNA is suitable as structural element for chromophore assemblies in future organic optoelectronic devices, such as solar cells.

Nanoparticle dispersions open up an ecofriendly route toward printable organic solar cells. They can be formed from a variety of organic semiconductors by using miniemulsions that employ surfactants to stabilize the nanoparticles in dispersion and to prevent aggregation. However, whenever surfactant-based nanoparticle dispersions have been used to fabricate solar cells, the reported performances remain moderate. In contrast, solar cells from nanoparticle dispersions formed by precipitation (without surfactants) can exhibit power conversion efficiencies close to those of state-of-the-art solar cells processed from blend solutions using chlorinated solvents. In this work, we use small-angle neutron scattering measurements and transient absorption spectroscopy to investigate why surfactant-free nanoparticles give rise to efficient organic solar cells. We show that surfactant-free nanoparticles comprise a uniform distribution of small semiconductor domains, similar to that of bulk-heterojunction films formed using traditional solvent processing. This observation differs from surfactant-based miniemulsion nanoparticles that typically exhibit core-shell structures. Hence, the surfactant-free nanoparticles already possess the optimum morphology for efficient energy conversion before they are assembled into the photoactive layer of a solar cell. This structural property underpins the superior performance of the solar cells containing surfactant-free nanoparticles and is an important design criterion for future nanoparticle inks.

The fabrication of organic solar cells with advanced multi-layer architectures from solution is often limited by the choice of solvents since most organic semiconductors dissolve in the same aromatic agents. In this work, we investigate multi-pass deposition of organic semiconductors from eco-friendly ethanol dispersion. Once applied, the nanoparticles are insoluble in the deposition agent, allowing for the application of further nanoparticulate layers and hence for building poly(3-hexylthiophene-2,5-diyl):indene-C60 bisadduct absorber layers with vertically graded polymer and conversely graded fullerene concentration. Upon thermal annealing, we observe some degrees of polymer/fullerene interdiffusion by means of X-ray photoelectron spectroscopy and Kelvin probe force microscopy. Replacing the common bulk-heterojunction by such a graded photo-active layer yields an enhanced fill factor of the solar cell due to an improved charge carrier extraction, and consequently an overall power conversion efficiency beyond 4%. Wet processing of such advanced device architectures paves the way for a versatile, eco-friendly and industrially feasible future fabrication of organic solar cells with advanced multi-layer architectures.

SummaryWe have investigated the adsorption of perylene-3,4,9,10-tetracarboxylic acid dianhydride (PTCDA) on the clean and on the oxygen pre-covered Cu(100) surface [referred to as (√2 × 2√2)R45° – 2O/Cu(100)] by scanning tunneling microscopy (STM) and low energy electron diffraction (LEED). Our results confirm the (4√2 × 5√2)R45° superstructure of PTCDA/Cu(100) reported by A. Schmidt et al. [J. Phys. Chem. 1995, 99,11770–11779]. However, contrary to Schmidt et al., we have no indication for a dissociation of the PTCDA upon adsorption, and we propose a detailed structure model with two intact PTCDA molecules within the unit cell. Domains of high lateral order are obtained, if the deposition is performed at 400 K. For deposition at room temperature, a significant density of nucleation defects is found pointing to a strong interaction of PTCDA with Cu(100). Quite differently, after preadsorption of oxygen and formation of the (√2 × 2√2)R45° – 2O/Cu(100) superstructure on Cu(100), PTCDA forms an incommensurate monolayer with a structure that corresponds well to that of PTCDA bulk lattice planes.

The formation of poly(p-phenylene-terephthalamide) (PPTA) by surface-assisted polymerization of terephthaloyl chloride (TPC) and p-phenylenediamine (PPD) on Ag-(111) has been studied by X-ray photoelectron spectroscopy (XPS) and scanning tunneling microscopy (STM). Analysis of the XPS data reveals that the polymer is formed in the (sub-) monolayer regime already at room temperature. Upon vacuum deposition of TPC onto the single-crystal surface, the carbonÀ chlorine bond is cleaved, and the polymerization proceeds via a pphenylene dicarbonyl species, which is presumably surface stabilized. This contrasts the reaction mechanism in solution, where the chlorine atom is expelled after a nucleophilic attack by the amine group. Annealing of the sample leads to desorption of residual PPD monomers, lateral ordering of the polymer chains, and further progress of the polymerization that can be followed by XPS. The chain length distribution of the polyamide, as extracted from the XP spectra, is consistent with the typical chain lengths found in STM images.

To improve charge carrier injection into or extraction from organic optoelectronic devices, electrically doped layers are often employed. Whereas n-doping of organic semiconductors has been widely used in vacuum processed optoelectronic devices, adequate solution processes to enable future device printing are underdeveloped. In this work, we study n-doping of 1,3,5-tris(1-phenyl-1H-benzimidazol-2-yl) benzene (TPBi) in a solution process, using sodium as the electron donor. Upon addition of elementary sodium to a clear TPBi/toluene solution, we observed a change in color, indicating charge carrier transfer between sodium and TPBi. The optical and electrical properties of doped and undoped TPBi were characterized in solution and in the corresponding thin-films. Electron Paramagnetic Resonance (EPR) measurements revealed an increase of the number of unpaired spins upon doping, indicating the presence of doping-induced charge carriers. Implementing TPBi : Na as electron extraction layers in organic solar cells, we found almost the same device performance as compared to state-of-the-art solar cells comprising zinc oxide electron extraction layers.