Micellization of a poly(ethylene oxide)-block-poly(4-vinylpyridine) (PEO45-b-P4VP28) copolymer in water during metalation (incorporation of gold compounds and gold nanoparticle formation) with three types of gold compounds, NaAuCl4, HAuCl4, and AuCl3, was studied using dynamic light scattering (DLS) and transmission electron microscopy (TEM). The transformations of the PEO45-b-P4VP28 block copolymer micelles in water were found to depend on a number of parameters including the thermal history of the as-prepared block copolymer, the type of the metal compound, and the metal loading. For the HAuCl4-filled PE045-b-P4VP28 micelles, the subsequent reduction with hydrazine hydrate results in a significant fraction of rodlike micelles, suggesting that slow nucleation (confirmed by the formation of the large gold nanoparticles) and facilitated migration of gold ions yields the ideal conditions for sphere-to-rod micellar transition.
Impregnation of hyper-cross-linked polystyrene (HPS) with tetrahydrofuran (THF) or methanol (ML) solutions containing platinic acid results in the formation of Pt(II) complexes within the nanocavities of HPS. Subsequent reduction of the complexes by H2 yields stable Pt nanoparticles with a mean diameter of 1.3 nm in THF and 1.4 nm in ML. The highest selectivity (98% at 100% conversion) measured during the catalytic oxidation of L-sorbose in water is obtained with the HPS-Pt-THF complex prior to H2 reduction. During an induction period of about 100 min, L-sorbose conversion is negligible while catalytic species develop in situ. The structure of the catalyst isolated after the induction period is analyzed by X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy. Electron micrographs reveal a broad distribution of Pt nanoparticles, 71% of which measure less than or equal to 2.0 nm in diameter. These nanoparticles are most likely responsible for the high catalytic activity and selectivity observed. The formation of nanoparticles measuring up to 5.9 nm in diameter is attributed to the facilitated intercavity transport and aggregation of smaller nanoparticles in swollen HPS. The catalytic properties of these novel Pt nanoparticles are highly robust, remaining stable even after 15 repeated uses.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.