This preliminary result demonstrated neither better alveolar ridge preservation nor enhanced bone formation of PRF in the extraction socket. The use of PRF revealed limited effectiveness by accelerated soft-tissue healing on the first 4 weeks.
The biphasic calcium phosphate (BCP) concept was introduced to overcome disadvantages of single phase biomaterials. Different composition ratios of BCP bioceramics have been studied, yet controversies regarding the effects of ratio on biomaterial behavior still exist. In this study, BCP scaffolds were prepared from nano hydroxyapatite (HA) and β-tricalcium phosphate (β-TCP) that were synthesized via a solid state reaction. Three different composition ratios of pure BCP and collagen-based BCP scaffolds (%HA/%β-TCP; 30/70, 40/60, and 50/50) were produced using a polymeric sponge method. Physical and mechanical properties of all materials and scaffolds were investigated. SEM showed overall distribution of both macropores (80-200 μm) and micropores (0.5-2 μm) with high interconnected porosities. Total porosity of pure BCP (90% ± 3%) was found to be higher than collagen-based BCP (85% ± 2%). It was observed that following sintering process, dimensional shrinkage of large scaffolds (39% ± 4%) was lower than small ones (42% ± 5%) and scaffolds with high HA ratios (50%) experienced higher dimensional changes than those with higher β-TCP (70%) ratios (45% ± 3% and 36% ± 1%, respectively). Compressive strength of both groups was less than 0.1 MPa and collagen coating had almost no influence on mechanical behavior. Further studies may improve the physical properties of these scaffolds and investigate their exact biological behaviors.
Fabrication of polycaprolactone (PCL)-chitosan (CS) three-dimensional (3D) scaffolds using the novel technique of melt stretching and multilayer deposition was introduced. In brief, firstly, the PCL-CS monofilaments containing 0% (pure PCL), 10%, 20% and 30% CS by weight were fabricated by melting and stretching processes. Secondly, the desired multilayer (3D) scaffolds were fabricated by arranging and depositing the filaments. Physical properties of the filaments and the scaffolds were evaluated. MC3T3-E1 cell lines were seeded on the scaffolds to assess their proliferation. A typical micro-groove pattern was found on the surfaces of pure PCL filaments due to stretching. The filaments of PCL-30%CS had the highest tendency of fracture during stretching and could not be used to form the scaffold. Increasing CS proportions tended to reduce the micro-groove pattern, surface roughness, tensile strength and elasticity of the filaments, whilst compressive strength of the PCL-CS scaffolds was not affected. The average pore size and porosity of the scaffolds were 536.90 ± 17.91 µm and 45.99 ± 2.8% respectively. Over 60 days, degradation of the scaffolds gradually increased (p > 0.05). The more CS containing scaffolds were found to increase in water uptake, but decrease in degradation rate. During the culture period, the growth of the cells in PCL-CS groups was significantly higher than in the pure PCL group (p < 0.05). On culture-day 21, the growth in the PCL-20%CS group was significantly higher than the other groups (p < 0.05). In conclusion, the PCL-20%CS scaffolds obtained the optimum results in terms of physical properties and cellular response.
The aim of this study was to evaluate the accuracy of cone-beam computed tomography (CBCT) for determining cortical thickness and the gray value, investigating its correlation with micro-computed tomography (CT) and histology analysis. Sixty-two bone samples from 4 anatomic regions of the jaw were analyzed. A radiographic surgical stent was used during CBCT and bone sample harvesting. The cortical thickness and gray value of the planned implant were evaluated by CBCT. Bone volumetric fractions, bone mineral density, and % porosity assessed by micro-CT and mineralized material by histology analysis from harvested bone samples were analyzed and assessed for the association with the CBCT using Pearson correlation. A correlation between cortical thickness measured from the CBCT and Micro-CT (r = 0.933, P < 0.01) was identified. There was no difference between gray values measured from the CBCT among regions, while bone density parameters from micro-CT and histologic analysis showed significant difference (P < 0.01) among regions. Bone density parameters from micro-CT and histologic analysis showed correlation with cortical thickness but not with the gray value. In conclusion, CBCT is highly accurate in linear measurements and demonstrated correlation with genuine bone density. However, the gray value could not demonstrate the true bone density according to a low correlation to bone density variable measured from micro-CT and histologic analysis.
This study aimed to evaluate in vitro biocompatibility of a composite of nanoscale biphasic calcium phosphate (BCP) and collagen (C) compared to pure BCP (P) in different composition ratios of nanohydroxyapatite to nano-β-tricalcium phosphate (HA/β-TCP). Each study group comprised of three ratios of BCP (30/70, 40/60, and 50/50). For evaluation of cellular response toward each ratio, mouse osteoblast (MC3T3-E1) cell line was cultivated on the scaffolds for 19 days. Analysis of cell proliferation, cell viability, cell attachment and morphology, alkaline phosphatase (ALP) activity, and osteocalcin synthesis were done on culture days 1, 3, 7, 13, 15, and 19, appropriately. The scanning electron microscopy showed that the osteoblasts attached successfully to scaffolds surfaces in both BCP groups and in all different ratios by spreading their filopodia and expressing similar viability that was confirmed by confocal laser scanning electron microscope. BCP scaffold (P3070) showed remarkable ALP activity, whereas BCP (P5050) showed highest osteocalcin activity. Collagen coating supported high cell proliferation on culture day 1 and possessed limited benefit restricted to early phase of cell differentiation. In conclusion, the fabricated nanoscale BCP scaffolds offered high biocompatibility and supported well the cell proliferation and differentiation regardless the composition ratio. Furthermore, higher ratio of TCP supported the early phase of cell proliferation, whereas higher HA ratio influenced the later phase. Finally, BCP scaffolds P5050 and C4060 were suggested as candidates for clinical applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.