Microstructured and near nanostructured Cr3C2–Ni–Cr–B–Si coatings were deposited on Inconel 718 superalloy by high‐velocity oxygen fuel thermal spray technique. The oxidation behavior of microstructured and near nanostructured Cr3C2–Ni–Cr–B–Si coated superalloy at 900°C in air for 50 cycles under cyclic heating and cooling conditions was studied. The kinetics of oxidation of both nanostructured and microstructured coated superalloy was analyzed by weight change measurement. It was noticed that the uncoated and coated alloy obey the parabolic rate law of oxidation. X‐ray diffraction, field‐emission scanning electron microscopy/energy dispersive x‐ray analysis, and elemental mapping techniques were used to analyze the oxidized samples of coated and uncoated samples. In the coated superalloy, iron, silicon, and titanium were oxidized in the inter‐splat region, whereas the splats which consist mainly of Ni and Cr remain unoxidized. Because of the formation of compact and adhesive thin NiO and Cr2O3 scale on the surface of the coating during oxidation, the developed nanostructured coated superalloy shows better oxidation resistance than the microstructured one.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.