We investigate the average power scaling of two diode-pumped Yb-doped fiber amplifiers emitting a diffraction-limited beam. The first fiber under investigation with a core diameter of 30 µm was able to amplify a 10 W narrow linewidth seed laser up to 2.8 kW average output power before the onset of transverse mode instabilities (TMI). A further power scaling was achieved using a second fiber with a smaller core size (23µm), which allowed for a narrow linewidth output power of 3.5 kW limited by stimulated Brillouin scattering (SBS). We mitigated SBS using a spectral broadening mechanism, which allowed us to further increase the output power to 4.3 kW only limited by the available pump power. Up to this power level, a high slope efficiency of 90% with diffraction-limited beam quality and without any sign of TMI or stimulated Raman scattering for a spectral dynamic range of higher than -80 dB was obtained.
In this contribution we investigate the transversal mode instability behavior of a ytterbium-doped commercial 20/400 fiber and obtain 2.9 kW of output power after optimizing the influencing parameters. In this context, we evaluate the influence of the bend diameter and the pump wavelength within the scope of the absorption length and the length of the fiber. Furthermore, with a newly developed fiber we report on 4.4 kW of single-mode output power at 40 cm bend diameter.
We report on a newly designed and fabricated ytterbium-doped large mode area fiber with an extremely low NA (~0.04) and related systematic investigations on fiber parameters that crucially influence the mode instability threshold. The fiber is used to demonstrate a narrow linewidth, continuous wave, single mode fiber laser amplifier emitting a maximum output power of 3 kW at a wavelength of 1070 nm without reaching the mode-instability threshold. A high slope efficiency of 90 %, excellent beam quality, high temporal stability, and an ASE suppression of 70 dB could be reached with a signal linewidth of only 170 pm.
Laser cooling of a solid is achieved when a coherent laser illuminates the material in the red tail of its absorption spectrum, and the heat is carried out by anti-Stokes fluorescence of the blue-shifted photons. Solid-state laser cooling has been successfully demonstrated in several materials, including rare-earth-doped crystals and glasses. Here we show the net cooling of high-purity Yb-doped silica glass samples that are fabricated with low impurities to reduce their parasitic background loss for fiber laser applications. The non-radiative decay rate of the excited state in Yb ions is very small in these glasses due to the low level of impurities, resulting in near-unity quantum efficiency. We report the measurement of the cooling efficiency as a function of the laser wavelength, from which the quantum efficiency of the Yb-doped silica is calculated.
We report on the optical refrigeration of ytterbium doped silica glass by >40 K starting at room temperature, which represents more than a two-fold improvement over the previous state-of-the-art. A spectroscopic investigation of the steady-state and time-dependent fluorescence was carried out over the temperature range 80 K to 400 K. The calculated minimum achievable temperature for our Yb3+ doped silica sample is ≈150 K, implying the potential for utilizing ytterbium doped silica for solid-state optical refrigeration below temperatures commonly achieved by standard Peltier devices.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.