Thermoplastic polysiloxane-based polyurethane (Si-TPU) has been attracting a great deal of attention because of the dual advantages of polysiloxane and polyurethane. However, the strength of Si-TPU with a traditional structure is low, and improvement is urgently needed for diverse applications. Herein, we design a polysiloxane-based soft segment (SS) with two urethane groups at the end of the polysiloxane chain, and then we prepare a series of Si-TPUs through a designed SS, isophorone diisocyanate and 1,4-butanediol. Such structural design improves the polarity of the SS and endows more regular hydrogen bonds to the polymer molecular chain. As a result, the prepared Si-TPUs exhibit a good microphase separation structure, unprecedentedly high strength, repeatable processing, noncytotoxicity, shape memory properties, and three-dimensional printing capabilities. Moreover, a maximum tensile strength of Si-TPUs can reach 20.3 MPa, exceeding that of other existing Si-based polymer materials. Si-TPUs show great potential for biomedical applications.
Polysiloxanes have attracted considerable attention in biomedical engineering, owing to their inherent properties, including good flexibility and biocompatibility. However, their low mechanical strength limits their application scope. In this study, we synthesized a polysiloxane-based polyurethane by chemical copolymerization. A series of thermoplastic polysiloxane-polyurethanes (Si-TPUs) was synthesized using hydroxyl-terminated polydimethylsiloxane containing two carbamate groups at the tail of the polymer chains 4,4′-dicyclohexylmethane diisocyanate (HMDI) and 1,4-butanediol as raw materials. The effects of the hard-segment content and soft-segment number average molecular weight on the properties of the resulting TPUs were investigated. The prepared HMDI-based Si-TPUs exhibited good microphase separation, excellent mechanical properties, and acceptable repeatable processability. The tensile strength of SiTPU-2K-39 reached 21.5 MPa, which is significantly higher than that of other flexible polysiloxane materials. Moreover, the tensile strength and breaking elongation of SiTPU-2K-39 were maintained at 80.9% and 94.6%, respectively, after three cycles of regeneration. The Si-TPUs prepared in this work may potentially be used in gas separation, medical materials, antifouling coatings, and other applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.