This study aimed to investigate the shear bond strength of an autopolymerizing resin to a nylon denture base polymer (Lucitone FRS: LT) subjected to different surface treatments, and the results thereof compared with a heat-polymerizing resin and a polycarbonate polymer. Specimens were divided into five groups according to the surface treatment method: polishing (#600), sandblasting, adhesive primer application (resin primer), sandblasting + adhesive primer application, and tribochemical coating (Rocatec system). Following which, specimens were subjected to a shear bond strength test and Si concentrations were measured using an electron probe microanalyzer (EPMA). On shear bond strength, that of LT with tribochemical coating was significantly higher than the other groups. On EPMA results, the surface of LT with tribochemical coating was found to be covered with a silica film. Therefore, findings in this study indicated that silica-coating by Rocatec system was effective in improving the bond strength of nylon denture base polymer to autopolymerizing repair resin.
The purpose of our study was to evaluate the effects of surface modifications on the bond strength between veneering porcelains and Yttria-stabilized tetragonal zirconia (Y-TZP). In a bond strength tests, the effect of control, 70 µm alumina-sandblasting, 30 µm and 110 µm silica-coating of the Y-TZP surface on bonding were evaluated with veneering porcelains. In addition, the effect of surface modification on the flexural strength of Y-TZP was also evaluated. The data was analyzed using one-way ANOVA and Tukey test. All specimens showed bond strength values in excess of 25 MPa, the minimum allowed by ISO9693. In addition, significantly differences were found between the control and the 30 µm silica-coated. On the other hand the flexural strength of Y-TZP does not significantly difference for any surface modification. These results indicate that silica-coating may provide an effective pre-treatment for this enhancement of the bond strength while maintaining the strength of Y-TZP.
This study evaluated the effectiveness of a simplified silica coating method (CoJet System) on the bonding strength of resin cements to dental alloy. Bonding strength of the specimens treated with metal primer after alumina sandblasting was compared with those treated with silica coating and silane coupling agent after alumina sandblasting. Furthermore, the influence of silane coupling agent on bonding strength was compared between one-liquid and two-liquid silane coupling agents. Measurement of shear bond strength before and after thermal cycling revealed that the group treated with silica coating in one step without alumina sandblasting yielded high bonding strength. As for the influence of silane coupling agent, treatment with two-liquid silane coupling agent achieved higher mean shear bond strength than with one-liquid silane coupling agent. Findings in this study indicated that silicatization by means of this simplified silica coating method was effective in improving the bonding strength to dental alloy.
the dentinal tubules. These results suggest that the reaction products produced by sequential treatment with acidic fluoride and LaCl3 and powdered apatite glass ceramics are able to effectively occlude dentinal tubules.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.