InGaN multi-quantum-well (MQW) structure laser diodes (LDs) fabricated from III-V nitride materials were grown by metalorganic chemical vapor deposition on sapphire substrates. The mirror facet for a laser cavity was formed by etching of III-V nitride films without cleaving. As an active layer, the InGaN MQW structure was used. The InGaN MQW LDs produced 215 mW at a forward current of 2.3 A, with a sharp peak of light output at 417 nm that had a full width at half-maximum of 1.6 nm under the pulsed current injection at room temperature. The laser threshold current density was 4 kA/cm2. The emission wavelength is the shortest one ever generated by a semiconductor laser diode.

High-brightness blue, green and yellow light-emitting diodes (LEDs) with quantum well structures based on III-V nitrides were grown by metalorganic chemical vapor deposition on sapphire substrates. The typical green LEDs had a peak wavelength of 525 nm and full width at half-maximum (FWHM) of 45 nm. The output power, the external quantum efficiency and the luminous intensity of green LEDs at a forward current of 20 mA were 1 mW, 2.1% and 4 cd, respectively. The luminous intensity of green LEDs (4 cd) was about 40 times higher than that of conventional green GaP LEDs (0.1 cd). Typical yellow LEDs had a peak wavelength of 590 nm and FWHM of 90 nm. The output power of yellow LEDs was 0.5 mW at 20 mA. When the emission wavelength of III-V nitride LEDs with quantum well structures increased from the region of blue to yellow, the output power decreased dramatically.

Superbright green InGaN single quantum well (SQW) structure light-emitting diodes (LEDs) with a luminous intensity of 12 cd were fabricated. The luminous intensity of these green InGaN SQW LEDs (12 cd) was about 100 times higher than that of conventional green GaP LEDs (0.1 cd). The output power, the external quantum efficiency, the peak wavelength and the full width at half-maximum of green SQW LEDs were 3 mW, 6.3%, 520 nm and 30 nm, respectively, at a forward current of 20 mA. The p-AlGaN/InGaN/n-GaN structure of green InGaN SQW LEDs were grown by metalorganic chemical vapor deposition on sapphire subsutrates.

InGaN multi-quantum-well-structure laser diodes (LDs) grown on GaN substrates were demonstrated. The LDs showed a small thermal resistance of 30 °C/W and a lifetime longer than 780 h despite a large threshold current density of 7 kA/cm2. In contrast, the LDs grown on a sapphire substrate exhibited a high thermal resistance of 60 °C/W and a short lifetime of 200 h under room-temperature continuous-wave operation.

High-power blue and violet light-emitting diodes (LEDs) based on III–V nitrides were grown by metalorganic chemical vapor deposition on sapphire substrates. As an active layer, the InGaN single-quantum-well-structure was used. The violet LEDs produced 5.6 mW at 20 mA, with a sharp peak of light output at 405 nm, and exhibited an external quantum efficiency of 9.2%. The blue LEDs produced 4.8 mW at 20 mA and sharply peaked at 450 nm, corresponding to an external quantum efficiency of 8.7%. These values of the output power and the quantum efficiencies are the highest ever reported for violet and blue LEDs.