Metal-organic frameworks, a new class of materials with high surface area and great porosity, have been widely applied in gas sorption. It is generally known that metal-organic framework 5 cannot be applied in aqueous phase since it is water sensitive. However, this work reveals that the derived material of metal-organic framework 5 is a good SPE sorbent that can be applied to aqueous phases. Metal-organic framework 5 was prepared and used as a SPE sorbent for the determination of polycyclic aromatic hydrocarbons in environmental matrices coupling with HPLC. The water treatment induced changes in the properties were investigated in detail. Even though metal-organic framework 5 is conversed to a second phase after water treatment, it still shows high extraction ability. Under the optimized experimental conditions, good sensitivity levels were achieved with low LODs ranging from 0.4 to 4.0 ng L(-1) and a linearity of 0.004-20 μg L(-1) (R(2) > 0.996) for the investigated polycyclic aromatic hydrocarbons. The method has been validated in the analysis of real water samples with recoveries in the range of 80.2-120.2% and RSDs in the range of 0.5-11.7%.
Phosphorus‐rich metal phosphides have very high lithium storage capacities, but they are difficult to prepare. A low‐temperature phosphorization method based on Mg reducing PCl3 in ZnCl2 molten salt at 300 °C is developed to synthesize phosphorus‐rich CuP2@C from a Cu‐MOF derived Cu@C composite. Abnormal oxidation of Cu by Zn2+ in the molten salt is observed, which leads to the porous honeycomb nanostructure and homogeneously distributed ultrafine CuP2 nanocrystals. The honeycomb CuP2@C exhibits excellent lithium storage performance with high reversible capacity (1146 mAh g−1 at 0.2 A g−1) and superior cycling stability (720 mAh g−1 after 600 cycles at 1.0 A g−1), showing the promising application of P‐rich metal phosphides in lithium ion batteries.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.