This paper investigates the effect of quenching and aging treatment on microstructure and abrasive wear of Ti-6Al-4V alloy. The as-received alloy was solution treated at 1339 K, then oil quenched, followed by aging at 823 K for 4 h (14,400 s). The microstructures of as-received and quench-aged specimens were characterized by using optical microscopy, scanning electron microscopy, energy dispersive spectroscopy, and electron backscattered diffraction techniques. The as-received specimen consisted of very fine a grains (average grain size 2 lm) with b phase uniformly dispersed throughout. The microstructure of the quenchaged specimen showed a plates (formed by the decomposition of a¢ during aging). The b phase precipitated out of a¢ martensite during aging and hence was dispersed uniformly in the a matrix. Ti-6Al-4V alloy was quench-aged to achieve maximum hardness with a view that the increased hardness would lead to an improvement in abrasive wear behavior. Two-body abrasive wear tests were carried out on the as-received and quench-aged specimens using pin-on-disk apparatus with SiC as abrasive media (150-grit size). The effect of sliding distance and normal load on the abrasive wear behavior was studied. The wear resistance of the as-received specimen was greater than that of quench-aged specimen, while hardness of the as-received specimen was lower than that of quench-aged specimen. The abrasive wear behavior of Ti-6Al-4V alloy has been explained based on morphology/microstructure of the alloy and the associated wear mechanism(s).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.