An efficient lignocellulosic biomass pre-treatment is a crucial step for the valorization of these kind of raw materials. Lignocellulosic biomass is a potentially valuable resource for transformation into biofuels and bio-based products. The use of ionic liquids as media for the biomass pre-treatment is an alternative method that follows the green chemistry concept. This work proposes a new methodology for wheat straw pre-treatment with the ionic liquid (IL) 1-ethyl-3-methylimidazolium acetate ([emim][OAc]), which allowed the production of cellulose, hemicellulose and lignin-rich fractions in a rapid and simple three-step fractionation process. Various temperatures (80-140 uC) and processing times (2-18 h) of the pretreatment were studied. The quantitative and qualitative analysis of each lignocellulosic biomass fraction was determined by FTIR measurements. The glucan content in recovered cellulose-rich fractions was investigated by enzymatic hydrolysis. The cellulose recovery dependence on the pre-treatment conditions was ascertained through regression analysis. The optimal result for the recovery of the cellulose-rich fraction was obtained at 140 uC during 6 h achieving 37.1% (w/w) of the initial biomass loading. For the same conditions, optimal results were also produced regarding the amount of glucan present (81.1% w/ w biomass ) in cellulose-rich fractions, the carbohydrate enrichment in the hemicellulose fraction (96% wt) and the purity of lignin (97% wt). The recovery of IL was performed after each pre-treatment and the obtained yields were up to 86% (w/w). The recovered ILs were analyzed by 13 C and 1 H NMR. The presence of value-added phenolic compounds in the recovered ILs was analyzed by capillary electrophoresis. Vanillin and its derivatives, as well as other lignin-based products, were identified.
h i g h l i g h t sA physical air-entraining method has been reported. The properties of high porosity cement-based foam materials have been investigated. Influence of water-cement ratio and HPMC on material properties has been analyzed. Pore structure formation mechanism has been clarified. a b s t r a c tHigh porosity cement-based foam materials were prepared through physical air-entraining method and the pore structure and the properties of materials were characterized. The results show that water-cement ratio and Hydroxypropyl Methyl Cellulose (HPMC) content have crucial influence on material properties. When the water-cement ratio was 0.9 and the content of HPMC was 0.4%, the cement-based foam material with the porosity of 94.33% and thermal conductivity value of 0.049 W/(m K) could be obtained. The formation mechanism of pore structure was analyzed that water-cement ratio and HPMC content affect the bubble film toughness which influence on material properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.