In this study, the cause of failure of a low-carbon steel pipe meeting standard KS D 3562 (ASTM A135), in a district heating system was investigated. After 6 years of operation, the pipe failed prematurely due to pitting corrosion, which occurred both inside and outside of the pipe. Pitting corrosion occurred more prominently outside the pipe than inside, where water quality is controlled. The analysis indicated that the pipe failure occurred due to aluminum inclusions and the presence of a pearlite inhomogeneous phase fraction. Crevice corrosion occurred in the vicinity around the aluminum inclusions, causing localized corrosion. In the large pearlite fraction region, cementite in the pearlite acted as a cathode to promote dissolution of surrounding ferrite. Therefore, in the groundwater environment outside of the pipe, localized corrosion occurred due to crevice corrosion by aluminum inclusions, and localized corrosion was accelerated by the large fraction of pearlite around the aluminum inclusions, leading to pipe failure.
Carbonaceous residues on copper pipes during the manufacturing process are known to be one of the main causes of pitting corrosion on copper pipes. This study examined the corrosion-inhibiting effect of benzotriazole (BTA) on C12200 copper pipes with carbonaceous film in synthetic tap water. In the absence of BTA, localized corrosion mechanisms due to galvanic corrosion, crevice corrosion, and oxygen-concentration cell were proposed in the boundary part of the carbonaceous film on the copper through X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) with energy dispersive spectrometer (EDS) analyses. Electrochemical tests showed that BTA inhibits corrosion by forming Cu−BTA complexes on all over the copper surface where carbonaceous film is present. BTA mitigates galvanic corrosion and crevice corrosion at the boundary of the carbonaceous film and suppresses the formation of oxygen-concentration cells through the formation of a Cu−BTA complex.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.