To develop reliable optical anti-counterfeiting materials, higher requirements are put forward for innovative anti-counterfeiting phosphors, which are hardly observed under natural light but recognizable under specified conditions. Herein, novel multimode...

No abstract

Transition‐metal phosphates have been widely applied as promising candidates for electrochemical energy storage and conversion. In this study, we report a simple method to prepare a N, F co‐doped mesoporous cobalt phosphate with rich‐oxygen vacancies by in‐situ pyrolysis of a Co‐phosphate precursor with NH4+ cations and F− anions. Due to this heteroatom doping, it could achieve a current density of 10 mA/cm2 at lower overpotential of 276 mV and smaller Tafel slope of 57.11 mV dec−1 on glassy carbon. Moreover, it could keep 92 % of initial current density for 35 h, indicating it has an excellent stability and durability. Furthermore, the optimal material applied in supercapacitor displays specific capacitance of 206.3 F g−1 at 1 A ⋅ g−1 and maintains cycling stability with 80 % after 3000 cycles. The excellent electrochemical properties should be attributed to N, F co‐doping into this Co‐based phosphate, which effectively modulates its electronic structure. In addition, its amorphous structure provides more active sites; moreover, its mesoporous structure should be beneficial to mass transfer and electrolyte diffusion.

No abstract